| 活性填料在聚碳硅烷先驱体转化陶瓷中的应用 |
| |
| 引用本文： | 谢征芳,陈朝辉,李永清,郑文伟,胡海峰,肖加余.活性填料在聚碳硅烷先驱体转化陶瓷中的应用[J].国防科技大学学报,2000,22(4):27-33. |
| |
| 作者姓名： | 谢征芳 陈朝辉 李永清 郑文伟 胡海峰 肖加余 |
| |
| 作者单位： | 国防科技大学航天与材料工程学院,湖南,长沙,410073 |
| |
| 基金项目： | 国家自然科学基金资助项目! ( 59682 0 0 9) |
| |
| 摘 要： | 比较了铝 (Al)、铬 (Cr)、二氢化钛 (TiH2 )和锆 (Zr)等活性填料在聚碳硅烷 (PCS)先驱体转化陶瓷中的应用。研究表明 ,在先驱体中加入活性填料能有效降低陶瓷素坯的气孔率 ,可与PCS气态裂解产物、游离碳和 (或 )N2 气氛反应生成新的化合物 ,提高PCS的陶瓷产率。活性填料的种类与含量对陶瓷烧成体的线收缩有较大的影响 ,Al、Cr能抑制烧成体的线收缩 ,其含量越高 ,线收缩越小。但是TiH2和Zr并不能抑制陶瓷烧成体的线收缩 ,其含量越高 ,线收缩越大。此外 ,活性填料的种类及含量对陶瓷烧成体的三点弯曲强度也有较大的影响。Al、Zr的含量越高 ,材料的强度也越大。但Cr和TiH2 的加入却使材料强度下降。认为Al是较好的活性填料。用X -衍射法 (XRD)分析了烧成产物的物相组成 ,扫描电子显微镜 (SEM)观察了陶瓷烧成体的断口形貌。
|
| 关 键 词： | 活性填料 聚碳硅烷 陶瓷 |
| 收稿时间： | 1999/12/22 0:00:00 |
Application of Active Fillers in the Preparation of Polycarbosilane Derived Ceramics |
| |
| XIE Zhengfang,CHEN Zhaohui,LI Yongqing,ZHENG Wenwei,HU Haifeng and XIAO Jiayu.Application of Active Fillers in the Preparation of Polycarbosilane Derived Ceramics[J].Journal of National University of Defense Technology,2000,22(4):27-33. |
| |
| Authors: | XIE Zhengfang CHEN Zhaohui LI Yongqing ZHENG Wenwei HU Haifeng and XIAO Jiayu |
| |
| Affiliation: | College of Aerospace and Materials Engineering, National Univ. of Defense Technology, Changsha 410073, China;College of Aerospace and Materials Engineering, National Univ. of Defense Technology, Changsha 410073, China;College of Aerospace and Materials Engineering, National Univ. of Defense Technology, Changsha 410073, China;College of Aerospace and Materials Engineering, National Univ. of Defense Technology, Changsha 410073, China;College of Aerospace and Materials Engineering, National Univ. of Defense Technology, Changsha 410073, China;College of Aerospace and Materials Engineering, National Univ. of Defense Technology, Changsha 410073, China |
| |
| Abstract: | The application of active fillers, Al, Cr, TiH 2 and Zr, in the preparation of polycarbosilane(PCS) derived ceramics was investigated. The results showed that the inclusion of active fillers could decrease the porosity of the green compacts effectively, increase ceramic yields of PCS by reacting with N 2, free carbon and/or gas volatile of PCS during pyrolysis to produce new compounds. It was found that Al and Cr could restrain the linear shrinkage of the green compact upon pyrolysis. While TiH 2 and Zr could not. The linear shrinkage got higher with increase of the volume ratio of TiH 2/PCS and Zr/PCS. It was also shown that the inclusion of Al and Zr could enhance the three point bending strength of the resulted ceramics with the strength of 212MPa and 104MPa when the volume ratio of Al/PCS and Zr/PCS were 60%vol, respectively, which were accordingly 3.3 and 1.6 times of that of the resulted ceramic in which active filler was not included. The inclusion of TiH 2 and Cr, however, could not enhance the strength. So Al was thought as the best among the four fillers. The phase compositions of pyrolysis products were analyzed using X ray diffraction(XRD). Fracture surfaces of specimens after three point bending tests were examined on the scanning electron microscope(SEM). |
| |
| Keywords: | active filler polycarbosilane(PCS) ceramics |