碳化硼表面金属化初步研究

为了降低碳化硼(B,C)与金属钎焊连接的温度,采用真空熔结Al基钎料的方法,在1000℃时对其进行了表面金属化处理,SEM和EDAX观察分析B4C与钎料结合断面的形貌和元素面分布,发现B4C与钎料界面发生了互扩散,界面结合致密,形成冶金结合.     

基于VCSEL实时点到点OFDM光信号在MMFs中的传输

通过实验,在使用未冷却直调3.63 GHz垂直腔面发射激光器的简单强度调制和直接检测系统中,首次证明在800 m OM2多模光纤上采用正交频分复用技术进行64 QAM(正交幅度调制)编码实现实时点到点通信,传输速度为11.25 Gb/s,功率损失1 d B。     

Combustion of B4C/KNO3 binary pyrotechnic system

Presented herein is an experimental study on the combustion of B4C/KNO3 binary pyrotechnic system.Combustion products were tested using X-ray diffraction(XRD),scanning electron microscopy(SEM),and energy dispersive spectrometer(EDS).According to the results of tests and CEA calculation,the combustion reaction equation was established.The flames and burning rates were recorded by a high speed camera and a spectrophotometer.The effect of B4C particle size on the thermal sensitivity of B4C/KNO3 was investigated by differential scanning calorimetry(DSC)techniques.In addition,a reliable method for calculating the flame temperature was proposed.Based on the results of experiments,the combustion reaction mechanism was briefly analyzed.The burning rate,flame temperature and thermal sensitivity of B4C/KNC3 increase with the decrease of B4C particle size.The mass ratio of B4C/KNO3 has a great effect on combustion properties.Oxidizer-rich compositions have low flame temperatures,low burning rates,and provide green light emission.The combustion reactions of fuel-rich compositions are vigorous,and the B4C/KNO3 with mass ratio of 25:75 has the highest burning rate and the highest flame temperature.     

Effect of transverse compression on the residual tensile strength of ultrahigh molecular weight polyethylene (Dyneema® SK-76) yarns

Ballistic impact induces complex stress states on fiber-based armor systems. During impact fibers undergo multiaxial loading which includes axial tension, axial compression, transverse compression, and transverse shear. Transverse compression induced by the projectile leads to permanent deformation and fibrillation of fibers resulting in degradation of material tensile strength. Previous work (Sockalingam et al. Textile Res. J 2018) has shown a reduction of 20% in the tensile strength of Dyneema® SK76 single fibers subjected to 77% nominal transverse compressive strains. Experimental investigation of quasi-static transverse compression on Dyneema® SK-76 yarns, unconstrained in the lateral direction, indicate an average of 4% reduction in tensile strength of yarns compressed to 77% nominal strains. In this work we use finite element modeling techniques to understand the difference in residual tensile strength between single fibers and yarns observed in laterally unconstrained transverse compression experiments. Finite element study of the transverse compression response of single fibers and yarns indicate that local strains developed in fibers within the yarn are much lower than the local strains developed in single fibers subjected to a given nominal strain and may explain the less reduction in strength observed in yarns.