基于GMAW堆焊成形的顺序焊道搭接量模型

焊道搭接量对保证三维堆焊成形过程的顺利进行以及成形件的精度都有较为重要的影响。根据焊接熔滴过渡的物理特性,建立了GMAW堆焊三维成形的顺序焊道搭接量模型,在此基础上计算了平整堆焊层的相邻两道焊道的理论间隔,采用实际焊接试验对理论模型进行了验证,得到的理论间隔为L=2/3W,并进一步计算了平整堆焊层的高度为h=H/1-θ,实际试验得到的结果与理论结果相吻合,从而为焊接成形过程的自动化奠定了基础。     

无电焊接材料的燃烧速度和燃烧温度研究

采用高放热性的铝热剂（CuO＋Al）并加入适当的添加剂,制备了便携式的无电焊接笔材料,其燃烧速度可控,且具有高的燃烧温度。研究了反应剂颗粒大小、混料均匀性等对无电焊接笔材料的燃烧性能的影响。结果表明：反应剂粒径对无电焊接笔的燃烧速度具有显著影响,随着反应剂粒径的增大,燃烧速度明显减慢。反应剂粒径和混料时间是影响单位时间放热量和混料均匀度的主要因素,因而对无电焊接笔的燃烧温度具有明显影响。在一定的混料时间下,反应物粉末具有最佳的混料均匀性。反应物粒径小且混料均匀性好的无电焊接笔材料,其燃烧温度高。     

焊接过程对焊接残余应力及残余变形的影响

采用热弹塑性有限元法 ,对直通焊和多人同时分段焊两种焊接过程的平板对接焊时焊接应力变形和圆柱壳板环缝的焊接变形进行比较 ,认为多人同时分段焊较直通焊无论在降低焊接残余应力还是焊接残余变形都具有非常显著的效果     

添加剂对无电焊接脱渣性及焊缝成形的影响

针对焊接熔渣严重影响无电焊接焊缝成形的问题,通过添加造渣剂组分,研究了添加剂对无电焊接熔渣脱渣性及焊缝成形的影响。测试结果表明:添加剂的加入,使得无电焊接熔渣体系中形成多种多元化合物,并均匀、弥散地分布在Al2O3基体之中,形成规则的片层状组织,具有较好的相容性,而且通过形成多种多元化合物,使得无电焊接熔渣中的Al2O3相含量明显降低,从而显著地改善了无电焊接的脱渣性和焊缝成形性能,焊接接头的拉伸强度得到明显提高。     

Effect of tool rotational speed on the particle distribution in friction stir welding of AA6092/17.5 SiCp-T6 composite plates and its consequences on the mechanical property of the joint

This study investigates the effect of tool rotational speed (TRS) on particle distribution in nugget zone (NZ) through quantitative approach and its consequences on the mechanical property of friction stir welded joints of AA6092/17.5 SiC_p-T6 composite. 6 mm thick plates are welded at a constant tool tilt angle of 2° and tool traverse speed of 1 mm/s by varying the TRS at 1000 rpm, 1500 rpm and 2000 rpm with a taper pin profiled tool. Microstructure analysis shows large quantity of uniformly shaped smaller size SiC particle with lower average particle area which are homogeneously distributed in the NZ. The fragmentation of bigger size particles has been observed because of abrading action of the hard tool and resulting shearing effect and severe stress generation due to the rotation of tool. The particles occupy maximum area in the matrix compared to that of the base material (BM) due to the redistribution of broken particles as an effect of TRS. The migration of particles towards the TMAZ-NZ transition zone has been also encountered at higher TRS (2000 rpm). The microhardness analysis depicts variation in average hardness from top to bottom of the NZ, minimum for 1500 rpm and maximum for 2000 rpm. The impact strength at 1000 rpm and 1500 rpm remains close to that of BM (21.6 J) while 2000 rpm shows the accountable reduction. The maximum joint efficiency has been achieved at 1500 rpm (84%) and minimum at 1000 rpm (68%) under tensile loading. Fractographic analysis shows mixed mode of failure for BM, 1000 rpm and 1500 rpm, whereas 2000 rpm shows the brittle mode of failure.