| 热交联聚碳硅烷纤维分步烧成工艺 |
| |
| 引用本文： | 王亦菲,范真祥,王军,李效东,雷绍增.热交联聚碳硅烷纤维分步烧成工艺[J].国防科技大学学报,2005,27(2):24-28. |
| |
| 作者姓名： | 王亦菲 范真祥 王军 李效东 雷绍增 |
| |
| 作者单位： | 国防科技大学,航天材料工程学院,湖南,长沙,410073 |
| |
| 基金项目： | 湖南省自然科学基金资助项目(03JJY4045) |
| |
| 摘 要： | 采用热交联工艺改进传统的空气不熔化工艺,在尽可能少引入氧的情况下实现聚碳硅烷纤维的不熔化处理。热交联处理后聚碳硅烷纤维在惰性气氛下进行分步烧成。通过元素分析、SEM、EDX、XRD等手段系统研究了分步烧成的工艺条件以及烧成后连续SiC纤维组成、微观结构及其性能。
|
| 关 键 词： | 热交联 聚碳硅烷纤维 连续烧成 |
| 文章编号： | 1001-2486(2005)02-0024-05 |
| 收稿时间： | 2004/10/27 0:00:00 |
| 修稿时间： | 2004年10月27 |
Study of the Step-by-step Sintering Process of the Polycarbosilane Fibers Cured by Thermal Cross-linking |
| |
| WANG Yifei,FAN Zhenxiang,WANG jun,LI Xiaodong and LEI Shaozeng.Study of the Step-by-step Sintering Process of the Polycarbosilane Fibers Cured by Thermal Cross-linking[J].Journal of National University of Defense Technology,2005,27(2):24-28. |
| |
| Authors: | WANG Yifei FAN Zhenxiang WANG jun LI Xiaodong and LEI Shaozeng |
| |
| Institution: | College of Aerospace and Materials Engineering, National Univ. of Defense Technology, Changsha 410073, China;College of Aerospace and Materials Engineering, National Univ. of Defense Technology, Changsha 410073, China;College of Aerospace and Materials Engineering, National Univ. of Defense Technology, Changsha 410073, China;College of Aerospace and Materials Engineering, National Univ. of Defense Technology, Changsha 410073, China;College of Aerospace and Materials Engineering, National Univ. of Defense Technology, Changsha 410073, China |
| |
| Abstract: | Thermal curing process was adopted to improve traditional air-process to reduce the oxygen content of the continuous silican carbide fibers by leading oxygen as less as possible to the fibers during the curing treatment. The polycarbosilane fibers cured by thermal curing are sintered step by step. The condition of sintering process and the element composition, microstructure and properties of the fibers are studied in details by element analysis, SEM,EDX,XRD. |
| |
| Keywords: | |