| 炮管内膛烧蚀磨损现象的分析 |
| |
| 引用本文： | 张振山,吴永峰.炮管内膛烧蚀磨损现象的分析[J].装甲兵工程学院学报,2003,17(2):67-70. |
| |
| 作者姓名： | 张振山 吴永峰 |
| |
| 作者单位： | 装甲兵工程学院控制工程系,北京,100072 |
| |
| 摘 要： | 目前国内外对火炮身管寿命的研究表明,火炮身管疲劳寿命低的问题已基本解决,而烧蚀磨损寿命已成为影响其寿命的主要因素。就此介绍了身管烧蚀磨损的特征和危害,并且分析了造成这些特征和危害的原因,最后就解决这些问题提出了相应的措施。
|
| 关 键 词： | 身管寿命 磨损 烧蚀 |
| 修稿时间： | 2002年7月15日 |
The Analysis of The Rubbing Abrasion and Erosion on The Barrel Bore |
| |
| ZHANG Zhen-shan WU Yong-feng.The Analysis of The Rubbing Abrasion and Erosion on The Barrel Bore[J].Journal of Armored Force Engineering Institute,2003,17(2):67-70. |
| |
| Authors: | ZHANG Zhen-shan WU Yong-feng |
| |
| Institution: | ZHANG Zhen-shan WU Yong-feng |
| |
| Abstract: | According to the present research of the barrel bore abroad and home, the lack of fatigue service life has basically been solved, And that the rubbing abrasion and erosion service life is the main reason effecting the service life. The paper presents the characters and harm of the problem and analyse the reasons. At last, some ways and methods to this problem were brought forward. |
| |
| Keywords: | service life abrasion erosion |
| 本文献已被 CNKI 维普 万方数据 等数据库收录！ |