复合材料修补金属裂损结构吸湿老化的试验与有限元分析

暴露在湿热环境中的复合材料修补金属裂损结构易吸湿老化,导致该结构性能下降,服役寿命缩短。为研究吸湿性对复合材料修补金属裂损结构修补效果和耐久性的影响,利用试验方法分析了吸湿性对复合材料胶补金属裂损结构及胶黏剂力学性能的影响;利用有限元方法评估了吸湿性对复合材料胶补金属裂损结构试验件修补效果和耐久性的影响。研究结果表明:吸湿后含穿透双边裂纹铝合金板玻璃纤维单面胶补试验件的疲劳裂纹扩展寿命和极限载荷的平均值分别下降为吸湿前的71%和90%;吸湿造成拉伸条件下复合材料胶补金属裂损结构胶层失效模式由内聚破坏为主转变为界面破坏为主;在"湿-热"老化30天后,E44/聚酰胺环氧树脂胶黏剂试验件吸水饱和,弹性模量下降为未老化前的40%,塑性应变超过了总应变的25%;有限元分析发现胶层损伤受吸湿影响明显,吸湿性加速了胶层损伤,且裂纹长度越长,加速作用越明显;同时吸湿使得裂纹尖端的J积分值急剧增大,导致修补结构的疲劳裂纹扩展寿命缩短,裂纹长度越长,吸湿性对于复合材料胶接修补效果的危害越严重。     

Does Terrorism Increase after a Natural Disaster? An Analysis based upon Property Damage

Does an emergency such as a natural disaster lead to a surge of terrorism? This paper contributes to the emerging literature on this issue. We consider the experience of 129 countries during the period 1998–2012 to determine the effect of a natural disaster on both domestic as well as transnational terrorism. We also control for endogeneity using expenditure on health care and land area in a country as instruments. In contrast to the existing literature, we measure the extent of terrorism by the value of property damage. The results indicate that after natural disasters, (a) transnational terrorism increases with a lag, and (b) a statistically significant impact on domestic terrorism is not observed.     

Relative Aging of Coherent Systems

In this article, we carry out the stochastic comparison between coherent systems through the relative aging order when component lifetimes are independent and identically distributed. We make use of the signature to characterize the structure of coherent systems, and derive several sufficient conditions under which the compared systems with the common size can be ordered in the sense of relative aging. Specially, we present some scenarios wherein the better a coherent system is, the faster it ages. Moreover, we discuss the relative aging of dual systems as well. Several numerical examples are provided to illustrate the theoretical results. © 2017 Wiley Periodicals, Inc. Naval Research Logistics 64: 345–354, 2017     

发动机粘接界面加速老化及寿命预测

介绍发动机粘接界面老化试验,根据其力学特性的变化,建立合适的数学模型,并估算出贮存寿命。     

Dynamic signatures and their use in comparing the reliability of new and used systems

The signature of a system with independent and identically distributed (i.i.d.) component lifetimes is a vector whose ith element is the probability that the ith component failure is fatal to the system. System signatures have been found to be quite useful tools in the study and comparison of engineered systems. In this article, the theory of system signatures is extended to versions of signatures applicable in dynamic reliability settings. It is shown that, when a working used system is inspected at time t and it is noted that precisely k failures have occurred, the vector s [0,1]^n‐k whose jth element is the probability that the (k + j)th component failure is fatal to the system, for j = 1,2,2026;,n ‐ k, is a distribution‐free measure of the design of the residual system. Next, known representation and preservation theorems for system signatures are generalized to dynamic versions. Two additional applications of dynamic signatures are studied in detail. The well‐known “new better than used” (NBU) property of aging systems is extended to a uniform (UNBU) version, which compares systems when new and when used, conditional on the known number of failures. Sufficient conditions are given for a system to have the UNBU property. The application of dynamic signatures to the engineering practice of “burn‐in” is also treated. Specifically, we consider the comparison of new systems with working used systems burned‐in to a given ordered component failure time. In a reliability economics framework, we illustrate how one might compare a new system to one successfully burned‐in to the kth component failure, and we identify circumstances in which burn‐in is inferior (or is superior) to the fielding of a new system. © 2009 Wiley Periodicals, Inc. Naval Research Logistics, 2009     

基于步进应力加速老化和改进Arrhenius模型的橡胶贮存寿命预测

为准确、快速地预测橡胶的贮存寿命,在步进高温应力加速老化试验的基础上,对不同加速温度下的加速系数进行计算,获得加速因子和绝对温度倒数的曲线,发现橡胶老化过程表现出非Arrhenius特性。针对非Arrhenius特性,引入幂指数因子,采用一种改进的Arrhenius模型对加速系数进行拟合。由对数反应速率与绝对温度倒数曲线的斜率,计算了改进Arrhenius模型在不同温度下的等效线性活化能,结果表明低温下活化能减小。建立低温下的老化寿命模型,对胶料在10℃,20℃和30℃下的老化寿命进行评估。评估结果表明,该模型可为相关高分子材料腐蚀过程中呈现的非Arrhenius特性的分析及寿命预测提供参考。     

矿物掺合料对GRC耐久性的影响

通过长达3年的标准养护试验及80℃热水加速老化试验,研究了矿物掺合料粉煤灰、硅灰对耐碱玻璃纤维增强普通硅酸盐水泥(GRC)耐久性的影响,并对矿物掺合料改善GRC耐久性的机理作了初步分析探讨。研究结果表明,粉煤灰和硅灰矿物掺合料可明显改善GRC的长期耐久性。     

资源与环境经济学教学实践与改革思路

资源与环境经济学教学的加强和发展要顺应时代的要求来,在注重实践教学环节的基础上深化教学改革。文章结合资源与环境经济学课程特点,在教学实践的基础上,提出了课程的改革思路,以期提高教学效果。     

关于S147 铝合金形变时效强化研究

本文研究了S147铝合金板材在形变时效处理各工艺阶段中的组织与性能。用扫描电镜观察分析了材料的断口形貌,并用薄膜试样在透射电镜下分析研究了该合金形变时效处理后的微观亚结构及过渡相析出物特征。结果表明,最佳形变时效处理可显著提高S147铝合金的强度及塑韧性,并能改善其过渡相析出过程及特征。     

Preservation of stochastic orders for random minima and maxima,with applications

It is shown, in this note, that the right spread order and the increasing convex order are both preserved under the taking of random maxima, and the total time on test transform order and the increasing concave order are preserved under the taking of random minima. Some inequalities and preservation properties in reliability and economics are given as applications. © 2003 Wiley Periodicals, Inc. Naval Research Logistics, 2004.