The effect of al particle size on thermal decomposition,mechanical strength and sensitivity of Al/ZrH2/PTFE composite

To study the thermal decomposition of Al/ZrH2/PTFE with different Al particle size as well as mechanical strength and impact sensitivity under medium and low strain rates, molding-vacuum sintering was adopted to prepare four groups of power materials and cylindrical specimens with different Al particle size. The active decomposition temperature of ZrH2 was obtained by TG-DSC, and the quasi-static me-chanics/reaction characteristics as well as the impact sensitivity of the specimen were studied respec-tively by quasi-static compression and drop-hammer test. The results show that the yield strength of the material decreased with the increase of the Al particle size, while the compressive strength, failure strain and toughness increased first and then decreased, which reached the maximum values of 116.61 MPa, 191％, and 119.9 MJ/m respectively when the Al particle size is 12—14μm because of particle size grading. The specimens with the highest strength and toughness formed circumferential open cracks and reacted partly when pressed. Those with developmental cracks formed inside did not react. It is considered that fracture of specimens first triggered initial reaction between Al and PTFE to release an amount of heat. Then ZrH2 was activated and decomposed, and participated in subsequent reaction to generate ZrC. The impact sensitivity of the specimens decreased with the increase of Al particle size.     

Experimental and numerical investigations of interface properties of Ti6Al4V/CP-Ti/Copper composite plate prepared by explosive welding

Explosive welding technique is widely used in many industries. This technique is useful to weld different kinds of metal alloys that are not easily welded by any other welding methods. Interlayer plays an important role to improve the welding quality and control energy loss during the collision process. In this paper, the Ti6Al4V plate was welded with a copper plate in the presence of a commercially pure titanium interlayer. Microstructure details of welded composite plate were observed through optical and scanning electron microscope. Interlayer-base plate interface morphology showed a wavy structure with solid melted regions inside the vortices. Moreover, the energy dispersive spectroscopy analysis in the interlayer-base interface reveals that there are some identified regions of different kinds of chemical equilibrium phases of Cu–Ti, i.e. CuTi, Cu₂Ti, CuTi₂, Cu₄Ti, etc. To study the mechanical properties of composite plates, mechanical tests were conducted, including the tensile test, bending test, shear test and Vickers hardness test. Numerical simulation of explosive welding process was performed with coupled Smooth Particle Hydrodynamic method, Euler and Arbitrary Lagrangian-Eulerian method. The multi-physics process of explosive welding, including detonation, jetting and interface morphology, was observed with simulation. Moreover, simulated plastic strain, temperature and pressure profiles were analysed to understand the welding conditions. Simulated results show that the interlayer base plate interface was created due to the high plastic deformation and localized melting of the parent plates. At the collision point, both alloys behave like fluids, resulting in the formation of a wavy morphology with vortices, which is in good agreement with the experimental results.