An interface shear damage model of chromium coating/steel substrate under thermal erosion load

The Cr-plated coating inside a gun barrel can effectively improve the barrel's erosion resistance and thus increase the service life.However,due to the cyclic thermal load caused by high-temperature gun-powder,micro-element damage tends to occur within the Cr coating/steel substrate interface,leading to a gradual deterioration in macro-mechanical properties for the material in the related region.In order to mimic this cyclic thermal load and,thereby,study the thermal erosion behavior of the Cr coating on the barrel's inner wall,a laser emitter is utilized in the current study.With the help of in-situ tensile test and finite element simulation results,a shear stress distribution law of the Cr coating/steel substrate and a change law of the interface ultimate shear strength are identified.Studies have shown that the Cr coating/steel substrate interface's ultimate shear strength has a significant weakening effect due to increasing temperature.In this study,the interfacial ultimate shear strength decreases from 2.57 GPa(no erosion)to 1.02 GPa(laser power is 160 W).The data from this experiment is employed to establish a Cr coating/steel substrate interface shear damage model.And this model is used to predict the flaking process of Cr coating by finite element method.The simulation results show that the increase of coating crack spacing and coating thickness will increase the service life of gun barrel.     

Visual SLAM in dynamic environments based on object detection

A great number of visual simultaneous localization and mapping (VSLAM) systems need to assume static features in the environment. However, moving objects can vastly impair the performance of a VSLAM system which relies on the static-world assumption. To cope with this challenging topic, a real-time and robust VSLAM system based on ORB-SLAM2 for dynamic environments was proposed. To reduce the influence of dynamic content, we incorporate the deep-learning-based object detection method in the visual odometry, then the dynamic object probability model is added to raise the efficiency of object detection deep neural network and enhance the real-time performance of our system. Experiment with both on the TUM and KITTI benchmark dataset, as well as in a real-world environment, the results clarify that our method can significantly reduce the tracking error or drift, enhance the robustness, accuracy and stability of the VSLAM system in dynamic scenes.     

车用磁流变减振器动力性能实验分析

MRF阻尼器结构简单、体积小、能耗低、反应迅速且阻尼力可调范围广, 已经成为新型履带车辆半主动悬挂系统优先选择的方案。基于磁流变液体本构关系的Bingham模型,对影响车用磁流变减振器的阻尼力的各种因素进行了综合分析。对自行研制的双出杆剪切阀式磁流变减振器进行了实验研究,获得了不同振幅、频率、电流强度下的阻尼力变化曲线,从不同的侧面获得了MRF阻尼器的动力性能。结合Hrovat限界最优半主动控制算法和车辆悬挂系统振动的半主动控制策略,仿真分析了磁流变阻尼器对整车振动的控制效果,并与LQR控制结果作了比较。     

坦克稳定器的神经滑模控制方法

针对坦克稳定器这一类非线性和不确定性的复杂控制对象,提出一种神经滑模控制方法。该方法将滑模控制与神经网络相结合,解决了控制系统跟踪性能和鲁棒性能之间的矛盾。系统中的滑模控制器保证了系统的快速跟踪性能;而神经网络具有很强的自学习功能,通过学习能够保证系统的稳定性,同时可对扰动和参数变化进行有效的抑制补偿,从而在不牺牲系统鲁棒性的同时达到削弱抖振的目的。从理论上证明了滑动平面的稳定性,并且通过仿真验证了该结果。仿真结果表明该设计方法优于经典设计,为实际设计提供了一种可行的新方法。     

可拓工程方法在效能-费用权衡中的应用

介绍可拓学及物元理论,提出用可拓工程方法对武器装备效能-费用进行权衡分析。建立了装备效费权衡分析的高阶复合物元模型,对初始效费方案进行了延拓,提出可拓特征集的概念。在此基础上,对效能-费用方案进行可拓聚类分析。     

基于组合媒质通道模型的地下目标成像

由于电磁波在穿越不同介质时会出现折射现象,因此在地下目标成像过程中,电磁波信号穿越从雷达到地下目标的组合通道的路径不是直线而是折线,此时利用常规的自由空间中的合成孔径成像方法已经不能对目标进行成像。基于电磁波的传播规律和地层有耗媒质的特性,提出了电磁波传输的组合通道模型,并将其应用到地下目标成像中。通过仿真比较可以看出,使用组合通道模型对地下目标成像效果有明显的改善,组合通道模型适用于对分层土壤中的地下目标成像。     

装备战场损伤的解析分析方法研究

为了提高装备战损模拟的效率,以蒙特卡洛方法为基础,构建了关于装备战损的解析模型。首先采用序贯法优化了仿真次数,以便以较少的仿真次数获得较高的仿真精度;分析了单因素对于装备损伤的影响,并建立了一元回归模型;采用正交试验分析了多因素之间的交互作用,并综合一元回归模型得出了装备战损的多元回归模型;最后结合弹着点分布模型与多元回归模型,建立了装备战损的解析模型,并通过实例验证了解析模型的正确性。     

通用雷达装备质量等级评定数学模型

在分析我军通用雷达装备质量等级划分的历史情况的基础上,依据装备的实际,从全寿命的观点出发,重点提出了进行质量等级划分和质量等级评定应考虑的要素,指出重新划分质量等级的依据,并首次提出了评定质量等级的数学模型。     

路面不平度的频谱分析及其AR模型

描述了路面不平度的统计特性,建立了AR模型。运用现代谱估计的方法对沙土地、硬土地和耕地等非人工路面的频谱特性进行了分析,得到了沙土地等3种路面的加速度功率谱和位移功率谱密度曲线图。结果表明,沙土地和耕地路面要好于硬土地路面,该结论与常识相符,验证了用AR模型法进行功率谱分析的可靠性和可行性。     

大型军车新型底盘自动集中润滑系统的研究与开发

开发了大型军车使用的新型底盘自动集中润滑系统(Chassis Centralized Lubrication System)。系统采用高效润滑泵、嵌入式控制系统及车内CAN总线网络扩展技术,大大提高了大型军车底盘的寿命,可有效地减少战场环境下的底盘故障。