高速微粒轰击45钢表面纳米化过程中铁素体相晶粒细化过程分析

利用高速微粒轰击技术在45钢表面制备了纳米晶,利用透射电镜（TEM）和X射线衍射（XRD）等分析技术对距表面不同深度的微观结构进行分析,研究铁素体相晶粒细化过程。结果显示：随着距表面距离的减小结构尺寸逐渐减小,在最表面形成了纳米晶层,平均晶粒尺寸约为15 nm。通过不同尺寸位错胞的逐步形成,以及位错墙不断向晶界演化,晶粒被细化为细小的纳米晶。     

Gas metal arc welding of high nitrogen stainless steel with Ar-N2-O2 ternary shielding gas

High nitrogen stainless steel with nitrogen content of 0.75％was welded by gas metal arc welding with Ar—N2-O2 ternary shielding gas. The effect of the ternary shielding gas on the retention and improvement of nitrogen content in the weld was identified. Surfacing test was conducted first to compare the ability of O2 and CO2 in prompting nitrogen dissolution. The nitrogen content of the surfacing metal with O2 is slightly higher than CO2. And then Ar—N2-O2 shielding gas was applied to weld high nitrogen stainless steel. After using N2-containing shielding gas, the nitrogen content of the weld was improved by 0.1 wt％. As N2 continued to increase, the increment of nitrogen content was not obvious, but the ferrite decreased from the top to the bottom. When the proportion of N2 reached 20％, a full austenitic weld was obtained and the tensile strength was improved by 8.7％. Combined with the results of surfacing test and welding test, it is concluded that the main effect of N2 is to inhibit the escape of nitrogen and suppress the ni-trogen diffusion from bottom to the top in the molten pool.     

Essentially Non-Oscillatory插值的分析与方法

在科学研究与工程计算中对插值的分析与方法理论已有很重要的应用,而对于ENO插值的方法与理论在大多教科书中却很少涉及,本文介绍ENO插值的应用及算法,为大学生们学习数值分析中的插值计算提供参考。     

15000m~3钢板贴壁油罐建设静态投资分析

以部队某保障基地油库军用柴油扩容工程采用钢板贴壁工艺新建的1座15 000 m3地下水封油池为例,从技术经济学角度对钢板贴壁油罐作了静态投资分析。该钢板贴壁油罐静态总投资1 756.95万元,其中占总投资比例最高者为地下工程建设,达到53.76%,库容投资1 171.30元/m3。结果表明:钢板贴壁油罐较地下水封石洞油罐整体经济效益明显;投资定额可供编制预算参考。     

基于分布实时多Agent技术的防空兵群指挥决策研究

探讨了防空兵群指挥决策的重要地位,依据现代高技术条件下防空兵群作战指挥的决策支持需求,研究并设计了防空兵群作战指挥决策支持系统的基本结构,重点研究了系统的人-机交互技术,阐述了Agent的元模型,详细论述了基于Agent的分布实时群体联盟体系,并对Agent的通信语言ACL消息结构进行分析且应用于联盟体系的通信传输,为构建防空兵群作战指挥决策支持系统的人机交互子系统提供技术准备。     

长杆射弹对钢纤维混凝土靶开坑特性的实验研究

为考察射弹对钢纤维混凝土靶的侵彻特性,采用57mm轻气炮,进行了小尺寸模拟射弹对钢纤维混凝土靶(钢纤维的体积分数为2%)的侵彻实验。实验中观察了钢纤维混凝土靶的开坑形状,测量了射弹的击靶速度,并且采用注沙法测出靶体的开坑体积,计算出射弹对靶体的侵彻体积,得到了长杆射弹的动能与侵彻体积的关系。引入射弹单位面积的冲击动能和靶体单位侵彻体积的冲击动能,结合钢纤维混凝土靶的实验数据,考察了两者之间的关系。     

Phenomenological modelling of flow behaviour of 20MnMoNi55 reactor pressure vessel steel at cryogenic temperature with different strain rates

In the present study a phenomenological constitutive model is developed to describe the flow behaviour of 20MnMoNi55 low carbon reactor pressure vessel (RPV) steel at sub-zero temperature under different strain rates. A set of uniaxial tensile tests is done with the variation of strain rates and temperature ranging from 10⁻⁴ s⁻¹ to 10⁻¹ s⁻¹ and -80 °C to −140 °C respectively. From the experimental data, family of flow curves at different temperatures and strain rates are generated and fitted exponentially. The strain rate and temperature dependence of the coefficients of the exponential flow curves are extracted from these curves and characterised through a general phenomenological constitutive coupled equation. The coefficients of this coupled equation are optimised using genetic algorithm. Finite element simulation of tensile tests at different strain rates and temperatures are done using this coupled equation in material model of Abaqus FEA software and validated with experimental results. The novelties of proposed model are: (a) it can predict precisely the flow behaviour of tensile tests (b) it is a simple form of equation where fitting parameters are both function of strain rate ratio and temperature ratio, (c) it has ability to characterize flow behaviour with decreasing subzero temperatures and increasing strain rates.     

Optimization of resistance spot brazing process parameters in AHSS and AISI 304 stainless steel joint using filler metal

The aim of this research study was to determine optimal resistance spot brazing parameters for joining between AHSS and AISI 304 stainless steel by using filler metal. The key parameters investigated in this study consist of the brazing current, electrode pressure and brazing time. The Taguchi method was applied to the design of experiments. Signal-to-Noise ratio was introduced in the study to identify optimal levels from the process where input parameters yield increased shear strength. Brazing was thus implemented with 5,000A brazing current, 0.70 MPa electrode pressure, and 1.50s brazing time. The maximum shear strength obtained was 54.31 N·mm⁻² in accordance with input parameter settings. In addition, Cu-rich phase and Ag_0.4Fe_0.6 intermetallic phases were found at the interface zone.     

船用60 kg级铸钢使用性能的试验研究

对船用60kg级铸钢进行多项使用性能试验,试验结果表明该铸钢常规力学性能和低温韧性全部合格,实物铸件解剖力学性能良好,与试块的解剖性能基本相当,具有良好的焊接性能,焊接接头的冲击和硬度试验达到技术条件规定的要求.