| 两相黄铜HPb59-1锻件的腐蚀缺陷分析 |
| |
| 引用本文： | 王双喜. 两相黄铜HPb59-1锻件的腐蚀缺陷分析[J]. 军械工程学院学报, 1998, 0(3) |
| |
| 作者姓名： | 王双喜 |
| |
| 作者单位： | 军械工程学院金属工艺教研室 石家庄 |
| |
| 摘 要： | 某军品的黄铜锻件在生产过程中产生了一种凹坑腐蚀缺陷。用金相方法对其显微组织进行研究,确定该组织缺陷由外氧化皮、内氧化区和脱锌带三部分组成,得出产生该缺陷的根本原因在于锻件酸洗时造成了缝隙腐蚀。
|
| 关 键 词： | 两相黄铜 缝隙腐蚀 锻件 酸洗 |
ANALYSIS OF CORROSION DEFECT ON THE SURFACE OF HPb59 -1 FORGING COMPONENT |
| |
| Wang Shuangxi. ANALYSIS OF CORROSION DEFECT ON THE SURFACE OF HPb59 -1 FORGING COMPONENT[J]. Journal of Ordnance Engineering College, 1998, 0(3) |
| |
| Authors: | Wang Shuangxi |
| |
| Affiliation: | Teaching and Research Section of Metal Process |
| |
| Abstract: | In the production process a kind of caved defect appears on the surfaces of forgingbrass components for an ordnance equipment. The microstructure is investigated by the opticalphotography technique. The experiment results show that the defect consists of three layers,i. e. outer oxide layer, inner oxide zone and dezinc band. Crivice corrosion is the principal, cause for the caved defect. |
| |
| Keywords: | brass crivice corrosion acid washing forging component |