铝合金-纯铝-钢复合板爆炸焊接试验及性能研究

通过设计爆炸焊接试验复合了铝合金-纯铝-钢爆炸复合板,对其界面形态、显微硬度及力学性能进行了研究。结果表明,铝合金-纯铝界面纯规则正弦波形,纯铝-钢复合板界面波形较小,铝合金-纯铝-钢复合板的界面剪切强度在75 MPa以上,爆炸复合过程中,纯铝与钢界面生成了金属间化合物,其界面处基体金属发生强烈的塑性变形。复合板变形及组织变化的结果造成复合板界面处的显微硬度最高,随着距界面距离的增加,两侧基体金属的硬度逐渐降低。     

917低磁钢与铝合金爆炸焊接复合实验研究

采用异种金属爆炸焊接复合技术 ,研制了 91 7低磁钢与LF5、LF2 1、LF1 1等铝合金的爆炸焊接复合板 ,并对该铝—钢复合板力学性能进行了实验研究 ,对复合界面进行了金相分析 .实验结果表明 ,该铝—钢复合板复合界面物理结合良好 ,其抗剪和抗弯强度满足实船使用要求     

Fabrication and analysis of TIG welding-brazing butt joints of in-situ TiB2/7050 composite and TA2

Lightweight hybrid structures of Al MMCs and titanium alloy dissimilar materials have great prospect in the defence industry application. So, it is necessary to join Al MMCs with Ti metal to achieve this structural design. In this work, in-situ TiB2/7050 composite and TA2 were firstly attempted to join by TIG welding-brazing technique. The result was that the intact welding-brazing butt joint was successfully fabricated. The joint presents dual characteristics, being a brazing on TA2 side and a welding on TiB2/7050 side. At brazing joint side, ER4043 filler metal effectively wets on TA2 under TIG heating condition, and a continuous interfacial reaction layer with 1—3μm is formed at welded metal/TA2 interface. The whole interfacial reaction layers are composed of Ti(AlSi)3 intermetallic compounds (IMCs), but their morphologies at the different regions present obvious distinguishes. The microhardness of the reaction layers is as much as 141—190 HV. At welding joints side, the fusion zone appears the equixaed crystal structure, and the grain sizes are much smaller than those of welded metal, which is attributed to the effect of TiB2 particulates from the melted TiB2/7050 on acceleration formation and inhibiting growth for the new crystal nucleus. The tensile test results show that average tensile strength of the optimal welding-brazing joint is able to achieve 138 MPa. The failure of the tensile joint occurs by quasi-cleavage pattern, and the cracks initiate from the IMCs layer at the groove surface of TA2 and propagate into the welded metal.     

2A12铝合金焊接接头超声冲击处理前后拉伸性能分析

为克服铝合金薄板焊接接头强度偏低、韧性不足的缺点,用ER5356焊丝对不同厚度的2A12铝合金板材进行了手工氩弧焊接,并采用超声冲击处理对焊接接头进行全覆盖强化处理。采用金相显微镜观察了处理和未处理焊接接头的显微组织结构,对接头的力学性能进行了测试分析,分析了超声冲击处理改善2A12铝合金焊接接头力学性能的机理。结果表明：铝合金焊接接头经超声冲击强化处理后,6 mm和4 mm厚板材对接接头的抗拉强度分别提高了17.4%和23.7%,延伸率分别提高了28%和44%,焊缝表层组织得到明显细化。分析认为：晶粒大幅细化、组织致密化和缺陷减少,是超声冲击处理改善铝合金焊接接头抗拉伸性能的主要原因。     

7A52铝合金便携式搅拌摩擦焊接头的组织与性能分析

采用便携式搅拌摩擦焊设备,对3mm厚的7A52铝合金薄板进行了焊接,对焊接头的显微组织和机械性能进行了观察测试。研究结果表明:焊接头可分为动态再结晶区、热-机影响区和母材3个区域,而没有明显的热影响区。动态再结晶区组织发生再结晶,生成细小的等轴晶粒;热-机影响区有塑性变形流线,且范围较窄;母材区保持着原来的轧制组织。接头硬度的最薄弱环节在热-机影响区。接头抗拉强度达到母材的70%左右,能够满足战场应急抢修的需求。     

Effects of nano-sized aluminum on detonation characteristics and metal acceleration for RDX-based aluminized explosive

Nano-sized aluminum(Nano-Al)powders hold promise in enhancing the total energy of explosives and the metal acceleration ability at the same time.However,the near-detonation zone effects of reaction between Nano-Al with detonation products remain unclear.In this study,the overall reaction process of 170 nm Al with RDX explosive and its effect on detonation characteristics,detonation reaction zone,and the metal acceleration ability were comprehensively investigated through a variety of experiments such as the detonation velocity test,detonation pressure test,explosive/window interface velocity test and confined plate push test using high-resolution laser interferometry.Lithium fluoride(LiF),which has an inert behavior during the explosion,was used as a control to compare the contribution of the reaction of aluminum.A thermochemical approach that took into account the reactivity of aluminum and ensuing detonation products was adopted to calculate the additional energy release by afterburn.Combining the numerical simulations based on the calculated afterburn energy and experimental results,the param-eters in the detonation equation of state describing the Nano-Al reaction characteristics were calibrated.This study found that when the 170 nm Al content is from 0％to 15％,every 5％increase of aluminum resulted in about a 1.3％decrease in detonation velocity.Manganin pressure gauge measurement showed no significant enhancement in detonation pressure.The detonation reaction time and reaction zone length of RDX/Al/wax/80/15/5 explosive is 64 ns and 0.47 mm,which is respectively 14％and 8％higher than that of RDX/wax/95/5 explosive(57 ns and 0.39 mm).Explosive/window interface velocity curves show that 170 nm Al mainly reacted with the RDX detonation products after the detonation front.For the recording time of about 10 μs throughout the plate push test duration,the maximum plate velocity and plate acceleration time accelerated by RDX/Al/wax/80/15/5 explosive is 12％and 2.9 μs higher than that of RDX/LiF/wax/80/15/5,respectively,indicating that the aluminum reaction energy significantly increased the metal acceleration time and ability of the explosive.Numerical simulations with JWLM explosive equation of state show that when the detonation products expanded to 2 times the initial volume,over 80％of the aluminum had reacted,implying very high reactivity.These results are significant in attaining a clear understanding of the reaction mechanism of Nano-Al in the development of aluminized explosives.     

Microstructure and pitting corrosion of armor grade AA7075 aluminum alloy friction stir weld nugget zone-Effect of post weld heat treatment and addition of boron carbide

Friction stir welding(FSW) of high strength aluminum alloys has been emerged as an alternative joining technique to avoid the problems during fusion welding.In recent times FSW is being used for armor grade AA7075 aluminum alloy in defense,aerospace and marine applications where it has to serve in non uniform loading and corrosive environments.Even though friction stir welds of AA7075 alloy possess better mechanical properties but suffer from poor corrosion resistance.The present work involves use of retrogression and reaging(RRA) post weld heat treatment to improve the corrosion resistance of welded joints of aluminum alloys.An attempt also has been made to change the chemical composition of the weld nugget by adding B4C nano particles with the aid of the FSW on a specially prepared base metal plate in butt position.The effects of peak aged condition(T6),RRA and addition of B4C nano particles on microstructure,hardness and pitting corrosion of nugget zone of the friction stir welds of AA7075 alloy have been studied.Even though RRA improved the pitting corrosion resistance,its hardness was slightly lost.Significant improvement in pitting corrosion resistance was achieved with addition of boron carbide powder and post weld heat treatment of RRA.     

Friction welding of AA6061 to AISI 4340 using silver interlayer

The present work pertains to the study on joining of AA6061 and AISI 4340 through continuous drive friction welding. The welds were evaluated by metallographic examination, X-ray diffraction, electron probe microanalysis, tensile test and microhardness. The study reveals that the presence of an intermetallic compound layer at the bonded interface exhibits poor tensile strength and elongation. Mg in AA6061 near to the interface is found to be favourable for the formation and growth of Fe2Al5 intermetallics. Introduction of silver as an interlayer through electroplating on AISI 4340 resulted in accumulation of Si at weld interface, replacing Mg at AA6061 side, thereby reducing the width of intermetallic compound layer and correspondingly increasing the tensile strength. Presence of silver at the interface results in partial replacement of Fe-Al based intermetallic compounds with Ag-Al based compounds. The presence of these intermetallics was confirmed by X-ray diffraction technique. Since Ag-Al phases are ductile in nature, tensile strength is not deteriorated and the silicon segregation at weld interface on AA6061 in the joints with silver interlayer acts as diffusion barrier for Fe and further avoids formation of Fe-Al based intermetallics. A maximum tensile strength of 240 MPa along with 4.9% elongation was obtained for the silver interlayer dissimilar metal welds. The observed trends in tensile properties and hardness were explained in relation to the microstructure.     

Characterization of magnetically impelled arc butt welded T11 tubes for high pressure applications

Magnetically impelled arc butt(MIAB) welding is a pressure welding process used for joining of pipes and tubes with an external magnetic field affecting arc rotation along the tube circumference. In this work, MIAB welding of low alloy steel(T11) tubes were carried out to study the microstructural changes occurring in thermo-mechanically affected zone(TMAZ). To qualify the process for the welding applications where pressure could be up to 300 bar, the MIAB welds are studied with variations of arc current and arc rotation time. It is found that TMAZ shows higher hardness than that in base metal and displays higher weld tensile strength and ductility due to bainitic transformation. The effect of arc current on the weld interface is also detailed and is found to be defect free at higher values of arc currents. The results reveal that MIAB welded samples exhibits good structural property correlation for high pressure applications with an added benefit of enhanced productivity at lower cost.The study will enable the use of MIAB welding for high pressure applications in power and defence sectors.     

横向运动板对长杆弹变形及运动影响的数值研究

利用Ls—DYNA软件对钨合金长杆弹垂直侵彻单层和双层横向运动钢板进行了数值计算。通过分析长杆弹的塑性变形、速度降、动能降和横向速度，得到了单层和双层板横向运动速度与影响长杆弹侵彻能力因素的关系。仿真结果表明：随着运动板速度的增加，运动板对长杆弹的侵蚀加剧，长杆弹的速度降、动能降增大；运动板相同速度下，虽然单层板的冲击能使长杆弹获得较大横向速度，但双层板比单层板对长杆弹的干扰效果更明显。     

焊接过程对焊接残余应力及残余变形的影响

采用热弹塑性有限元法 ,对直通焊和多人同时分段焊两种焊接过程的平板对接焊时焊接应力变形和圆柱壳板环缝的焊接变形进行比较 ,认为多人同时分段焊较直通焊无论在降低焊接残余应力还是焊接残余变形都具有非常显著的效果     

Effect of welding processes on mechanical and microstructural characteristics of high strength low alloy naval grade steel joints

Naval grade high strength low alloy(HSLA) steels can be easily welded by all types of fusion welding processes. However, fusion welding of these steels leads to the problems such as cold cracking, residual stress, distortion and fatigue damage. These problems can be eliminated by solid state welding process such as friction stir welding(FSW). In this investigation, a comparative evaluation of mechanical(tensile, impact,hardness) properties and microstructural features of shielded metal arc(SMA), gas metal arc(GMA) and friction stir welded(FSW) naval grade HSLA steel joints was carried out. It was found that the use of FSW process eliminated the problems related to fusion welding processes and also resulted in the superior mechanical properties compared to GMA and SMA welded joints.     

Experimental investigation of Tie6Ale4V titanium alloy and 304L stainless steel friction welded with copper interlayer

The basic principle of friction welding is intermetallic bonding at the stage of super plasticity attained with self-generating heat due to friction and finishing at upset pressure. Now the dissimilar metal joints are especially popular in defense, aerospace, automobile, bio-medical,refinery and nuclear engineerings. In friction welding, some special alloys with dual phase are not joined successfully due to poor bonding strength. The alloy surfaces after bonding also have metallurgical changes in the line of interfacing. The reported research work in this area is scanty. Although the sound weld zone of direct bonding between Tie6Ale4 V and SS304 L was obtained though many trials, the joint was not successful. In this paper, the friction welding characteristics between Tie6Ale4 V and SS304 L into which pure oxygen free copper(OFC) was introduced as interlayer were investigated. Boxe Behnken design was used to minimize the number of experiments to be performed. The weld joint was analyzed for its mechanical strength. The highest tensile strength between Tie6Ale4 V and SS304 L between which pure copper was used as insert metal was acquired. Micro-structural analysis and elemental analysis were carried out by EDS, and the formation of intermetallic compound at the interface was identified by XRD analysis.     

板的弹塑性弯曲有限元分析中的分层法

论述了板的弹塑性弯曲有限元分析方法 ,对屈服函数的选取作了分析 ,采用分层方法 ,着重分析了对板的弹塑性切线刚度矩阵的建立 ,所论述的分层计算方法对其它非线性板弯曲的有限元计算具有一定的参考价值     

Dissimilar friction stir spot welding of AA2024-T3/AA7075-T6 aluminum alloys under different welding parameters and media

This paper studies the friction stir spot welding of AA2024-T3/AA7075-T6 Al alloys in the ambient and underwater environments by clarifying the nugget features,microstructure,fracture and mechanical properties of the joints.The results show that the water-cooling medium exhibits a significant heat absorption capacity in the AA2024-T3/AA7075-T6 welded joint.Nugget features such as stir zone width,circular imprints,average grain sizes,and angular inter-material hooking are reduced by the water-cooling effect in the joints.Narrower whitish(intercalated structures)bands are formed in the under-water joints while Mg2Si and Al2CuMg precipitates are formed in the ambient and the underwater welded joints respectively.An increase in tool rotational speed(600-1400 rpm)and plunge depth(0.1-0.5 mm)increases the tensile-shear force of the welded AA2024-T3/AA7075-T6 joints in both the ambient and underwater environments.The maximum tensile-shear forces of 5900 N and 6700 N were obtained in the ambient and the underwater welds respectively.     

Comparative study on transverse shrinkage,mechanical and metallurgical properties of AA2219 aluminium weld joints prepared by gas tungsten arc and gas metal arc welding processes

Aluminium alloy AA2219 is a high strength alloy belonging to 2000 series. It has been widely used for aerospace applications, especially for construction of cryogenic fuel tank. However, arc welding of AA2219 material is very critical. The major problems that arise in arc welding of AA2219 are the adverse development of residual stresses and the re-distribution as well as dissolution of copper rich phase in the weld joint.These effects increase with increase in heat input. Thus, special attention was taken to especially thick section welding of AA2219-T87 aluminium alloy. Hence, the present work describes the 25 mm-thick AA2219-T87 aluminium alloy plate butt welded by GTAW and GMAW processes using multi-pass welding procedure in double V groove design. The transverse shrinkage, conventional mechanical and metallurgical properties of both the locations on weld joints were studied. It is observed that the fair copper rich cellular(CRC) network is on Side-A of both the weldments. Further, it is noticed that, the severity of weld thermal cycle near to the fusion line of HAZ is reduced due to low heat input in GTAW process which results in non dissolution of copper rich phase. Based on the mechanical and metallurgical properties it is inferred that GTAW process is used to improve the aforementioned characteristics of weld joints in comparison to GMAW process.     

High strain rate deformation of explosion-welded Ti6Al4V/pure titanium

Multilayer materials are widely used in military, automobile and aerospace industries. In this paper, the response of an explosion-welded Ti6Al4V/pure titanium with a flat interface to dynamic loading is investigated. An SHPB apparatus is used. Then, the dynamic behaviour of a bimetal sample is explored with a DIC system coupled to the SHPB. Result indicates that in the bimetal sample pure titanium is deformed and failed before Ti6Al4V. The stress curve of the sample shows two different peaks in a striker velocity higher than the 18.3 m/s. When the incident wave encounters the interface of the Ti6Al4V/pure titanium sample, only a small fraction of the wave is reflected owing to similar impedance. Using the direct interpretation stress-strain curve is unreasonable in this case because of unhomogenised plastic deformation. The microstructure of the sample is investigated after loading. An adiabatic shear band is formed in the pure titanium side before failure, and the interface of the sample remains intact under different loading conditions. The FEM simulation result for the sample is in good agreement with experimental observations.     

Microstructure,mechanical and corrosion behavior of high strength AA7075aluminium alloy friction stir welds-Effect of post weld heat treatment

High strength aluminium alloy AA7075(Al-Zn-Mg-Cu) is a precipitate hardenable alloy widely used in the aerospace,defense,marine and automobile industries.Use of the heat treatable aluminium alloys in all these sectors is ever-increasing owing to their excellent strength-toweight ratio and reasonably good corrosion resistance.The shortage in corrosion resistance,however,usually poses negative concern about their reliability and lifetime when they service in the variable marine environments.These alloys also exhibit low weldability due to poor solidification microstructure,porosity in fusion zone and lose their mechanical properties when they are welded by fusion welding techniques.Friction stir welding(FSW) is a reliable technique to retain the properties of the alloy as the joining takes place in the solid state.The welds are susceptible to corrosion due to the microstructural changes in the weld nugget during FSW.In this work,the effect of post weld treatments,viz.,peak aging(T6) and retrogression reaging(RRA),on the microstructure,mechanical properties and pitting corrosion has been studied.Friction stir welding of 8 mm-thick AA7075 alloy was carried out.The microstructural changes of base metal and nugget zone of friction stir welds were studied using optical microscopy,scanning electron microscopy and transmission electron microscopy.Tensile and hardness test of base metal and welds has been carried out.Pitting corrosion resistance was determined through dynamic polarization test.It was observed that the hardness and strength of weld were observed to be comparatively high in peak aged(T6) condition but the welds showed poor corrosion resistance.The resistance to pitting corrosion was improved and the mechanical properties were maintained by RRA treatment.The resistance to pitting corrosion was improved in RRA condition with the minimum loss of weld strength.     

Effect of tool pin profile on microstructure and tensile properties of friction stir welded dissimilar AA 6061e AA 5086 aluminium alloy joints

Joints between two different grades of aluminium alloys are need of the hour in many light weight military structures.In this investigation,an attempt has been made to join the heat treatable(AA 6061) and non-heat treatable(AA 5086) aluminium alloys by friction stir welding(FSW)process using three different tool pin profiles like straight cylindrical,taper cylindrical and threaded cylindrical.The microstructures of various regions were observed and analyzed by means of optical and scanning electron microscope.The tensile properties and microhardness were evaluated for the welded joint.From this investigation it is founded that the use of threaded pin profile of tool contributes to better flow of materials between two alloys and the generation of defect free stir zone.It also resulted in higher hardness values of 83 HV in the stir zone and higher tensile strength of 169 MPa compared to other two profiles.The increase in hardness is attributed to the formation of fine grains and intermetallics in the stir zone,and in addition,the reduced size of weaker regions,such as TMAZ and HAZ regions,results in higher tensile properties.     

Investigation on the process parameters of TIG-welded aluminum alloy through mechanical and microstructural characterization

Multi-pass TIG welding was conducted on plates (15×300×180 mm3) of aluminum alloy Al-5083 that usually serves as the component material in structural applications such as cryogenics and chemical processing industries. Porosity formation and solidification cracking are the most common defects when TIG welding Al-5083 alloy, which is sensitive to the welding heat input. In the experiment, the heat input was varied from 0.89 kJ/mm to 5 kJ/mm designed by the combination of welding torch travel speed and welding current. Tensile, micro-Vicker hardness and Charpy impact tests were executed to witness the impetus response of heat input on the mechanical properties of the joints. Radiographic inspection was performed to assess the joint's quality and welding defects. The results show that all the specimens displayed inferior mechanical properties as compared to the base alloy. It was established that porosity was progressively abridged by the increase of heat input. The results also clinched that the use of me-dium heat input (1-2 kJ/mm) offered the best mechanical properties by eradicating welding defects, in which only about 18.26% of strength was lost. The yield strength of all the welded specimens remained unaffected indicated no influence of heat input. Partially melted zone (PMZ) width also affected by heat input, which became widened with the increase of heat input. The grain size of PMZ was found to be coarser than the respective grain size in the fusion zone. Charpy impact testing revealed that the absorbed energy by low heat input specimen (welded at high speed) was greater than that of high heat input (welded at low speed) because of low porosity and the formation of equiaxed grains which induce better impact toughness. Cryogenic (-196 C) impact testing was also performed and the results corroborate that impact properties under the cryogenic environment revealed no appreciable change after welding at designated heat input. Finally, Macro and micro fractured surfaces of tensile and impact specimens were analyzed using Stereo and Scanning Electron Microscopy (SEM), which have supported the experimental findings.