Fabrication and analysis of TIG welding-brazing butt joints of in-situ TiB2/7050 composite and TA2

Lightweight hybrid structures of Al MMCs and titanium alloy dissimilar materials have great prospect in the defence industry application. So, it is necessary to join Al MMCs with Ti metal to achieve this structural design. In this work, in-situ TiB2/7050 composite and TA2 were firstly attempted to join by TIG welding-brazing technique. The result was that the intact welding-brazing butt joint was successfully fabricated. The joint presents dual characteristics, being a brazing on TA2 side and a welding on TiB2/7050 side. At brazing joint side, ER4043 filler metal effectively wets on TA2 under TIG heating condition, and a continuous interfacial reaction layer with 1—3μm is formed at welded metal/TA2 interface. The whole interfacial reaction layers are composed of Ti(AlSi)3 intermetallic compounds (IMCs), but their morphologies at the different regions present obvious distinguishes. The microhardness of the reaction layers is as much as 141—190 HV. At welding joints side, the fusion zone appears the equixaed crystal structure, and the grain sizes are much smaller than those of welded metal, which is attributed to the effect of TiB2 particulates from the melted TiB2/7050 on acceleration formation and inhibiting growth for the new crystal nucleus. The tensile test results show that average tensile strength of the optimal welding-brazing joint is able to achieve 138 MPa. The failure of the tensile joint occurs by quasi-cleavage pattern, and the cracks initiate from the IMCs layer at the groove surface of TA2 and propagate into the welded metal.     

复合材料层合结构的非线性传热分析

基于一阶热层合理论,考虑材料非线性的影响,建立了复合材料层合结构非线性传热分析的热层合理论及其有限元方程.通过数值算例研究了材料非线性对反对称复合材料层合板瞬态温度场的影响.     

焊条粘结剂及烘焙温度对药皮吸潮性的影响

通过试验研究了改进水玻璃及焊条烘焙温度对焊条药皮吸潮行为的影响.结果表明,在水玻璃中加入防水剂和/或丙烯酸甲酯,以及水玻璃低碱化处理均能明显提高焊条药皮的耐吸潮性;对于不同类型的水玻璃,通过选择适当的烘焙温度可有效地防止药皮吸潮.     

粉末涂料聚酯树脂性能研究

在合成粉末涂料聚酯树脂配方中,着重研究了醇、酸对聚酯树脂玻璃化温度的影响,同时将合成产品进行表征,结果表明,合成产品的主要性能指标与国际同类产品相近。     

粉末涂料聚酯树脂合成研究

在合成粉末涂料聚酯树脂的配方中,重点研究了催化剂、抗氧剂、酸值、醇的损失对聚酯树脂玻璃化温度的影响,并将合成产品进行表征,主要性能指标与美国同类产品接近。     

高含钛量碳化硅纤维的研制

本文采用一种聚钛硅氧烷与聚碳硅烷反应,制得了Ti/Si摩尔比为0.10的聚钛碳硅烷。该聚合物具有良好的成丝性与稳定性,经熔融纺丝,再经不熔化处理后,在氮气气氛保护下1300℃热处理后制得了高含钛量的碳化硅纤维。文中对聚钛硅氧烷的合成与结构,它与聚碳硅烷的反应过程及聚钛碳硅烷的热分解特性进行了分析与研究。     

微型计算机在复合材料强度准则研究中的应用

文中论述了运用微型计算机(IBM-PC)进行复合材料强度准则研究的方法,包括强度包络线绘制、双向加载数据采集及实验数据处理等,同时还研究了如何确定双向试验中的破坏载荷值,并在分析实例中提供了较详细的数据。     

抗超高速撞击多层结构复合材料研究

本文介绍了抗超高速撞击多层结构复合材料的设计、制备和实验,并对结果进行了讨论,实验证明,以SiC陶瓷基复合材料为防护层、以空心微珠或多孔变密度复合材料为缓冲层、以编织物复合材料为结构层的多层结构复合材料,具有面密度低、抗撞击速度范围宽、抗撞击性能好的特点。     

抗磨添加剂与电弧喷涂耐磨涂层间的协同效应

研究了2种φ2mm粉芯丝材电弧喷涂Fe-Cr-Ni涂层和7Crl3涂层以及与2种典型润滑油抗磨添加剂的协同效应,并借助X光电子能谱(XPS)研究了其协同作用机理.结果表明DBP和ZDDP润滑油抗磨添加剂能明显地改善电弧喷涂Fe-Cr-Ni涂层和7Cr13涂层的抗磨性.添加剂DBP能显著地降低2种电弧喷涂涂层/GCr15摩擦副的摩擦系数,但ZDDP抗磨添加u剂的减摩效果不太显著.在含DBP和ZDDP添加剂油润滑条件下,涂层磨痕表面形成了摩擦化学反应膜.     

聚氨酯型复合推进剂的性能研究

本文研究聚氨酯型复合推进剂的力学性能和燃烧性能,给出了提高推进剂力学性能的有效途径,测试了推进剂燃烧性能的基本特征参数,采用光电子能谱(ESCA)对这种复合推进剂的界面作用机理进行了微观探讨.