自动化电弧喷涂路径偏移间距的优化模型

基于电弧喷涂沉积丘的轮廓呈高斯分布的假设,并结合实验结果,建立了电弧喷涂沉积丘轮廓的数学模型,由此推导出了自动化喷涂过程中平行路径偏移间距这一重要参量的优化模型。该模型为合理规划自动化喷涂的路径提供了依据。     

新型钢-混凝土组合板的力学性能研究

以加劲肋形式、组合板厚度和栓钉布置为参数,进行了9块新型组合板的力学性能试验.试验结果表明,组合板的正截面承载力可按基于修正平截面假定的极限状态计算;组合板的跨中挠度,可在按现行规范计算的基础上,加上考虑界面滑移影响的附加变形值予以修正.     

921A钢在海水中腐蚀的力学化学效应

为了研究弹性应力和弹塑性应变对921A船体钢在模拟海水中腐蚀行为的影响,采用自制的载荷-电化学实验装置对921A钢在载荷与腐蚀介质协同作用时的开路电位、动电位极化曲线和电化学阻抗谱等电化学性能进行了测试,并由电化学阻抗谱拟合得到的电荷传递电阻定义载荷下的腐蚀速率修正因子,将实验得到的腐蚀速率修正因子与理论值进行了对比。结果表明:弹性拉应力与弹性压应力对力学化学效应的影响具有对称性。力学化学效应随着弹性应力的增大而增大,随着弹塑性应变的增大先增大后减小。弹塑性应变对力学化学效应的影响远远大于弹性应力的影响。在研究范围内,弹塑性应变引起的腐蚀电位负移量最大为62.6 mV,相应的腐蚀速率修正因子高达4.113,而弹性应力引起的腐蚀电位负移量最大为24.5 mV,相应的腐蚀速率修正因子为1.746。由此可见,应力应变对921A钢在海水中腐蚀行为的影响不容忽视。     

几种防锈液对T52钢在酸性介质中耐蚀性的影响

研究了几种防锈液对T52(10Ti热)钢在Ph=5.0酸性水溶液中耐蚀性能的影响.用线性极化和交流阻抗法对这些防锈液的耐蚀性能进行了综合评估,试验结果表明:亚硝酸钠类、含氨基和羧基的有机化合物类两种防锈液的耐蚀性能较好;并用动电位扫描法对上述防锈液的作用机理进行了初步探讨,试验表明:上述防锈液主要是抑制电极的阳极过程.     

“9·11”世贸大楼坍塌原因数值分析

数值分析表明,"9·11"恐怖袭击事件造成纽约世贸大楼的内部竖向承重钢结构的防火保护层在爆炸中严重脱落,火灾高温使钢材强度大幅度降低,导致着火层群柱失稳,上部巨大的冲击荷载把下层柱逐层压渍,引发连续坍塌.最后对超高层建筑的结构设计提出建议.     

扭转约束对无防火保护钢柱抗火性能影响分析

应用ANSYS软件计算了钢柱在标准升温模式下的温度场,然后利用ANSYS的耦合分析模块,将温度场导入结构分析,分析了不同约束下轴心受压钢柱在温度升高时的力学反应,同时考虑了荷载比以及长细比对不同约束钢柱抗火性能的影响.研究表明:扭转约束钢柱的抗火性能要优于柱端没有扭转约束的简支柱;当钢柱长细比系数在30以内时,扭转约束...     

单囊式空气弹簧参数计算

建立了带辅助气室单囊式空气弹簧的力学模型 ,推导出了空气弹簧垂向刚度和自振频率的计算公式     

Experimental investigation on anti-penetration performance of polyurea-coated ASTM1045 steel plate subjected to projectile impact

In this study, the anti-penetration performance of polyurea/ASTM1405-steel composite plate subjected to high velocity projectile was analyzed. Two kinds of modified polyurea material (AMMT-053 and AMMT-055) were selected and a ballistic impact testing system including speed measuring target system and high-speed camera was designed. This experiment was conducted with a rifle and 5.8 mm projectile to explore the effects by the polyurea coating thickness, the polyurea coating position and the glass-fiber cloth on the anti-penetration performance of polyurea/ASTM1405-steel composite plate. The result showed that the effects of polyurea coating position were different between two types of polyurea, and that the effects of glass-fiber position were disparate between two types of polyurea as well. For AMMT-053 polyurea material, it was better to be on front face than on rear face; whereas for AMMT-055 pol-yurea, it was better to be on rear surface although the difference was very subtle. Additionally, formulas had been given to describe the relationship between the effectiveness of polyurea and the thickness of polyurea coating. In general, AMMT-055 had better anti-penetration performance than AMMT-053. Furthermore, five typical damage modes including self-healing, crack, local bulge, spallation and local fragmentation were defined and the failure mechanism was analyzed with the results of SHPB test. Additionally, the bonding strength played an important role in the anti-penetration performance of polyurea/steel composite plate.     

钢筋钢纤维混凝土既有裂缝梁中钢纤维阻裂作用有限元分析

通过建立钢筋钢纤维混凝土既有裂缝梁和钢筋混凝土既有裂缝梁的有限元分析模型,借助ANSYS分析了两种梁在荷载作用下的裂缝尖端处应力、裂缝宽度增幅和挠度并作出对比。分析结果表明钢纤维对裂缝开展有很好的阻止作用,而且能明显缓和裂缝尖端处应力,减小梁的挠度。     

钢筋混凝土外粘钢板结构裂缝的有限元数值模拟

随着高技术武器的不断发展,防护工程正面临着前所未有的威胁和挑战,新型防护结构及材料已经成为研究的热点。针对这一实际背景,运用ANSYS大型有限元软件,采用数值模拟的方法对普通钢筋混凝土结构和外粘钢板混凝土结构在相同均布面荷载作用下的变形、钢筋应力以及结构裂缝的开展情况进行了比较。结果表明外粘钢板的钢筋混凝土结构能够大大增强结构的抗力,并且有效的抑制了裂缝的开展。