SiC纤维表面CVD SiC涂层对其单丝强度的影响

采用化学气相沉积(CVD, Chemical Vapor Deposition)工艺在KD-I型SiC纤维表面制备了SiC涂层,选择2h、4h、6h和8h四个时间点研究了沉积时间对纤维性能的影响.结果表明:具有CVD SiC涂层的SiC纤维较无涂层的纤维来说强度有所下降;在所研究的沉积时间范围内,随着沉积时间的增加,涂层的厚度有所增加,涂层由不连续的岛状转变为连续层状,纤维的单丝强度出现了先升后降的趋势.     

华东烧结模型的数学计算(Ⅱ)

通过热力学分析和数学计算，讨论颗粒呈现面心立方堆积方式时，华东烧结模型中膨胀机制和收缩机制对烧结体总表面能的作用和总孔隙度比变化的影响，计算表明烧结过程中收缩机制占主导地位。     

超细干粉自动灭火装置在民用建筑中的应用前景分析

指出了超细干粉和超细干粉自动灭火装置的技术特点,并通过与其他自动灭火系统的比较,分析了超细干粉自动灭火装置在民用建筑中的应用前景。     

陶瓷/金属梯度热障涂层的制备及性能评价

为了评价陶瓷/金属梯度热障涂层的性能,设计了4种涂层方案和2种基体材料(1Cr18Ni9Ti和2Cr13).利用单枪单送粉器成功地制备了线性梯度涂层.通过观察涂层的微观结构、测量涂层的抗热震性能和热残余应力来评价涂层的性能.利用扫描电镜对各种陶瓷涂层的微观结构进行了观察和分析,利用X射线能谱分析得到了陶瓷梯度涂层试样中的不同区域的衍射图.热震试验表明,梯度涂层比非梯度涂层具有更好的抗热震性能.采用钻孔法对不同涂层方案进行了残余应力的测量,结果表明,压应力出现在1Cr18Ni9Ti基体材料上,而拉应力出现在2Cr13基体材料上.     

热障涂层厚度及其涂敷下材料内部缺陷的红外定量识别

针对热障涂层结构材料红外定量检测存在的不足,提出基于脉冲相位的LM(LevenbergMarquardt)识别算法。针对研究问题,建立了轴对称圆柱坐标下热障涂层结构材料的瞬态导热模型,利用有限体积法计算出检测表面的温度场,经快速傅里叶变换得到检测表面的相位分布,分析待检测参数对检测表面相位差的影响。以相位为识别条件,采用LM反演算法对热障涂层厚度及其涂敷下材料内部缺陷位置大小进行定量识别,并采用数值实验方法验证了基于相位的LM识别方法的有效性。     

An interface shear damage model of chromium coating/steel substrate under thermal erosion load

The Cr-plated coating inside a gun barrel can effectively improve the barrel's erosion resistance and thus increase the service life.However,due to the cyclic thermal load caused by high-temperature gun-powder,micro-element damage tends to occur within the Cr coating/steel substrate interface,leading to a gradual deterioration in macro-mechanical properties for the material in the related region.In order to mimic this cyclic thermal load and,thereby,study the thermal erosion behavior of the Cr coating on the barrel's inner wall,a laser emitter is utilized in the current study.With the help of in-situ tensile test and finite element simulation results,a shear stress distribution law of the Cr coating/steel substrate and a change law of the interface ultimate shear strength are identified.Studies have shown that the Cr coating/steel substrate interface's ultimate shear strength has a significant weakening effect due to increasing temperature.In this study,the interfacial ultimate shear strength decreases from 2.57 GPa(no erosion)to 1.02 GPa(laser power is 160 W).The data from this experiment is employed to establish a Cr coating/steel substrate interface shear damage model.And this model is used to predict the flaking process of Cr coating by finite element method.The simulation results show that the increase of coating crack spacing and coating thickness will increase the service life of gun barrel.     

Storage life prediction under pre-strained thermally-accelerated aging of HTPB coating using the change of crosslinking density

In order to predict the storage life of a certain type of HTPB (hydroyl-terminated polybutadiene) coating at 25 C and analyze the influence of pre-strain on the storage life, the accelerated aging tests of HTPB coating at 40 C, 50 C, 60 C, 70 C with the pre-strain of 0%, 3%, 6%, 9%, respectively were carried out. The variation regularity of the change of crosslinking density was analyzed and the aging model of HTPB coating under pre-strained thermally-accelerated aging was proposed. The storage life of HTPB coating at 25 C was estimated by using the Berthelot equation as the end point of the aging life with a 30% decrease in maximum elongation. The results showed that the change of crosslinking density of HTPB coating increased with the increase of aging temperature and aging time, and decreased with the in-crease of pre-strain. Under 0% pre-strain, the relationship between the change of crosslinking density of HTPB coating and the aging time can be described by the logarithmic model with the confidence probability greater than 99%.The stress relaxation phenomenon existed under 3%, 6% and 9% pre-strained aging. The aging model considering chemical aging and pre-strain was established with the confidence probability greater than 90%. The storage life of HTPB coating was 15.2935 years at 25 C under 0% pre-strain, which was reduced by 13.9007%, 75.6949% and 89.7859% under 3%, 6% and 9% pre-strain, respectively. The existence of pre-strain has a serious impact on the storage life of HTPB coating, therefore, the pre-strain should be avoided as much as possible during the actual storage.     

Buckling analysis of embedded graphene oxide powder-reinforced nanocomposite shells

In this study, the buckling analysis of a Graphene oxide powder reinforced (GOPR) nanocomposite shell is investigated. The effective material properties of the nanocomposite are estimated through Halpin-Tsai micromechanical scheme. Three distribution types of GOPs are considered, namely uniform, X and O. Also, a first-order shear deformation shell theory is incorporated with the principle of virtual work to derive the governing differential equations of the problem. The governing equations are solved via Galerkin's method, which is a powerful analytical method for static and dynamic problems. Comparison study is performed to verify the present formulation with those of previous data. New results for the buckling load of GOPR nanocomposite shells are presented regarding for different values of circumfer-ential wave number. Besides, the influences of weight fraction of nanofillers, length and radius to thickness ratios and elastic foundation on the critical buckling loads of GOP-reinforced nanocomposite shells are explored.     

铝合金表面涂覆隐身吸波涂层脱落原因分析

通过对某装备车体外脱落隐身吸波涂层样品的表面形貌、截面形貌、元素组成及含量分析,发现吸波涂层和Al2O3钝化层之间没有化学结合键,只存在物理吸附和机械结合,在外部环境的作用下,很容易引起隐身吸波涂层的脱落。     

添加型防静电涂料的研究进展

对添加型防静电涂料的组成、导电机理、导电填料的研究状况进行了综述,重点论述了导电填料的研究重点和发展方向.白色和浅色导电填料是未来添加型防静电涂料的重点研究对象.