Storage life prediction under pre-strained thermally-accelerated aging of HTPB coating using the change of crosslinking density

In order to predict the storage life of a certain type of HTPB (hydroyl-terminated polybutadiene) coating at 25 C and analyze the influence of pre-strain on the storage life, the accelerated aging tests of HTPB coating at 40 C, 50 C, 60 C, 70 C with the pre-strain of 0%, 3%, 6%, 9%, respectively were carried out. The variation regularity of the change of crosslinking density was analyzed and the aging model of HTPB coating under pre-strained thermally-accelerated aging was proposed. The storage life of HTPB coating at 25 C was estimated by using the Berthelot equation as the end point of the aging life with a 30% decrease in maximum elongation. The results showed that the change of crosslinking density of HTPB coating increased with the increase of aging temperature and aging time, and decreased with the in-crease of pre-strain. Under 0% pre-strain, the relationship between the change of crosslinking density of HTPB coating and the aging time can be described by the logarithmic model with the confidence probability greater than 99%.The stress relaxation phenomenon existed under 3%, 6% and 9% pre-strained aging. The aging model considering chemical aging and pre-strain was established with the confidence probability greater than 90%. The storage life of HTPB coating was 15.2935 years at 25 C under 0% pre-strain, which was reduced by 13.9007%, 75.6949% and 89.7859% under 3%, 6% and 9% pre-strain, respectively. The existence of pre-strain has a serious impact on the storage life of HTPB coating, therefore, the pre-strain should be avoided as much as possible during the actual storage.     

Transverse relaxation characteristic and stress relaxation model considering molecular chains of HTPB coating based on pre-strained thermal aging

In order to accurately describe the transverse relaxation characteristic and stress relaxation modulus of HTPB coating during pre-strain thermal aging process, a one month thermal aging test was carried out at 70 C with pre-strain of 0％, 3％, 6％ and 9％, respectively. The low-field 1H NMR and stress relaxation modulus tests were carried out for HTPB coating at different aging stages. The stress relaxation model considering the molecular chains was proposed according to the changes of crosslinking chain and dangling chain of HTPB coating during pre-strain aging. The results showed that with the increase of aging time, the decay rate of transverse relaxation curve became faster, the transverse relaxation time decreased, the value of combined parameter qMrl increased, the proportion of crosslinking chain decreased, while the proportion of dangling chain increased. Moreover, the stress relaxation modulus increased, the crosslinking network structure of HTPB coating became denser and the degree of cross-linking increased. At the initial aging stage, the pre-strain will destroy the crosslinking network structure of HTPB coating to a certain extent. With the increase of aging time, the effect of pre-strain will gradually weaken and the influence of aging on materials will gradually increase. The correlations between the stress relaxation model considering the molecular chains and the test results were more than 0.9950, which can accurately describe the stress relaxation modulus of HTPB coating during the pre-strain thermal aging process.     

端羟基聚丁二烯热分解系统研究

本文采用热分析—气相色谱-质潜联用技术和红外光谱法系统地研究了端羟基聚丁二烯(HTPB)热分解行为与气体产物组成,考察了影响HTPB热分解的几种因素,推测了HTPB热分解的可能机理。