纳米SiC晶须增强铜基纳米复合材料摩擦学性能研究

采用粉末冶金法制备了添加纳米SiC晶须（n-SiCw）的铜基纳米复合材料（SiCw／Cu）。研究了复合材料的显微组织、密度、硬度与n-SiCw含量之间的关系，通过球／盘式摩擦磨损试验机研究了SiCw／Cu复合材料的摩擦磨损性能。结果表明：随n-SiCw含量增加，基体中孔隙增多，并出现n-SiCw的偏聚，复合材料的密度减小，硬度增加；当n-SiCw含量为0．3wt％时，材料的减摩、耐磨性能最好；SiCw／Cu复合材料的磨损机制为疲劳磨损和磨粒磨损，并以疲劳磨损为主。     

Friction stir surfacing of cast A356 aluminiumesilicon alloy with boron carbide and molybdenum disulphide powders

Good castability and high strength properties of Ale Si alloys are useful in defence applications like torpedoes,manufacture of Missile bodies,and parts of automobile such as engine cylinders and pistons.Poor wear resistance of the alloys is major limitation for their use.Friction stir processing(FSP) is a recognized surfacing technique as it overcomes the problems of fusion route surface modification methods.Keeping in view of the requirement of improving wear resistance of cast aluminiumesilicon alloy,friction stir processing was attempted for surface modification with boron carbide(B4C) and molybdenum disulfide(Mo S2) powders.Metallography,micro compositional analysis,hardness and pin-on-disc wear testing were used for characterizing the surface composite coating.Microscopic study revealed breaking of coarse silicon needles and uniformly distributed carbides in the A356 alloy matrix after FSP.Improvement and uniformity in hardness was obtained in surface composite layer.Higher wear resistance was achieved in friction stir processed coating with carbide powders.Addition of solid lubricant Mo S2 powder was found to improve wear resistance of the base metal significantly.     

Influence of yttrium on microstructure and properties of Ni–Al alloy coatings prepared by laser cladding

Ni–Al alloy coatings with different Y additions are prepared on 45^# medium steel by laser cladding. The influence of Y contents on the microstructure and properties of Ni–Al alloy coatings is investigated using X-ray diffraction, scanning electron microscopy, electron probe microanalyzer, Vickers hardness tester, friction wear testing machine, and thermal analyzer. The results show that the cladding layers are mainly composed of NiAl dendrites, and the dendrites are gradually refined with the increase in Y additions. The purification effect of Y can effectively prevent Al₂O₃ oxide from forming. However, when the atomic percent of Y addition exceeds 1.5%, the extra Y addition will react with O to form Y₂O₃ oxide, even to form Al₅Y₃O₁₂ oxide, depending on the amount of Y added. The Y addition in a range of 1.5–3.5 at.% reduces the hardness and anti-attrition of cladding layer, but improves obviously its wear and oxidation resistances.     

润滑油纳米铜添加剂及其对不同粗糙度表面的减摩自修复行为

采用KBH4液相还原法制备了纳米铜添加剂,采用透射电子显微镜对纳米铜添加剂进行了表征,通过摩擦磨损试验机测试了纳米铜添加剂对4种不同粗糙度摩擦表面所表现的抗磨减摩性能,并对不同的磨损表面进行了光学显微镜和能谱分析。结果表明:纳米铜添加剂为分散性能稳定的20nm的球形颗粒;纳米铜添加剂具有良好的抗磨减摩性能,尤其是对于光滑的摩擦表面,与基础油相比,可使摩擦因数降低24%。纳米铜添加剂还具有良好的自修复性能,摩擦过程中,能够在摩擦表面形成一层高弹性低硬度的自修复膜,自修复效果对于光滑的摩擦表面更为显著。     

纳米SiO_2在润滑油中的高温摩擦学性能

采用多功能SRV试验机考察了纳米SiO2在菜籽油中的高温摩擦学性能,利用表面轮廓仪观察磨损表面形貌。结果表明,在恒定负荷试验中,纳米SiO2能明显改善菜籽油的高温减摩抗磨性能,在500℃时,摩擦因数仅为0.16,磨损量降低了80%以上。在连续加载的高温试验中,当试验温度为200℃时,纳米SiO2对菜籽油的减摩抗磨性能没有明显的改善;而当试验温度达到500℃时,纳米SiO2能明显地改善菜籽油的减摩抗磨性能,在大负荷(500N)的情况下更为突出。     

45钢表面激光熔覆Ni35合金涂层的组织及性能

为了修复45钢磨损装备零件,采用激光熔覆工艺在45钢表面制备了Ni35合金涂层。利用扫描电镜（SEM）、能谱分析仪（EDS）、X射线衍射仪、显微硬度计和磨损试验机分析了熔覆层的显微组织,测试了涂层的硬度和耐磨性能。结果表明：熔覆层由γ-Ni和Ni3B两相组成;熔覆层中存在平面晶、胞状晶、枝晶等多种形态;Ni35熔覆层的硬度为450HV,熔覆层的耐磨性是基体的2.86倍。     

Feasibility of surface-coated friction stir welding tools to join AISI 304 grade austenitic stainless steel

An attempt is made to develop the tools that are capable enough to withstand the shear, impact and thermal forces that occur during friction stir welding of stainless steels. The atmospheric plasma spray and plasma transferred arc hardfacing processes are employed to deposit refractory ceramic based composite coatings on the Inconel 738 alloy. Five different combinations of self-fluxing alloy powder and 60% ceramic reinforcement particulate mixtures are used for coating. The best friction stir welding tool selected based on tool wear analysis is used to fabricate the austenitic stainless steel joints.     

磁控溅射工艺对CrN基复合涂层微观结构及摩擦学性能的影响

采用闭合场非平衡磁控溅射技术在不锈钢基体上制备了不同质量分数Mo的CrMoN复合涂层。采用X射线衍射仪（XRD）、扫描电子显微镜（SEM）、能谱仪（EDX）和光电子能谱仪（XPS）,系统分析了CrMoN复合涂层的相结构、表面形貌、成分、原子化合价价态等,结果表明：添加Mo后,CrMoN涂层的择优取向由CrN涂层的（220）转变为（200）,CrMoN涂层中的Mo原子取代了CrN晶格中的Cr原子,形成（Cr,Mo）N置换固溶体。采用Nano Test 600硬度测试仪测定了CrMoN复合涂层的纳米硬度,结果表明：由于CrN相和MoN两种硬相的协同作用,使得CrMoN复合涂层的纳米硬度值增大。采用多功能摩擦磨损试验机测定了CrN涂层及CrMoN复合涂层的摩擦因数,结果表明：CrMoN复合涂层的摩擦因数低于CrN涂层,磨损过程中由于摩擦热反应生成大量MoO3,使得复合膜的摩擦因数降低,起到了一定的润滑效果,降低了磨损量。     

球磨时间对纳米SiO_2/Cu复合材料摩擦学性能的影响

采用球磨法与热压烧结工艺制备了添加w（n-SiO2）=1.0%的铜基纳米复合材料。通过球盘式摩擦磨损试验机测试了复合材料的摩擦磨损性能,采用排水法和场发射扫描电镜（FSEM）研究了复合材料的致密度、显微组织和磨损形貌。结果表明：球磨可提高复合材料的致密度,改善n-SiO2在铜基体中的分散均匀性;随球磨时间的增加,复合材料的动摩擦因数和磨损量先减小后增加,球磨10 h复合材料具有较低的摩擦因数和磨损量,磨损机理主要为磨料磨损。     

Effect of nano powder (Al2O3-CaO) addition on the mechanical properties of the polymer blend matrix composite

This work describes the preparation and study of the properties of composite nanoparticles prepared by the sol-gel method which consists of two materials (Al₂O₃-CaO), and study the effect of these nanoparticles on the mechanical behavior of a polymer blend (EP 4% + 96% UPE). The powder was evaluated by X-ray diffraction analysis, scanning electron microscopy analysis (SEM), particle size analysis, and energy dispersive X-ray analysis (EDX). The mechanical behavior of the composite material was assessed by tensile test, bending test and hardness test. The evaluation results of the composite nanoparticles showed good distribution of the chemical composition between aluminum oxide and calcium oxide, smoothness in particles' size at calcination in high and low temperatures, formation of different shapes of nanoparticles and different (kappa and gamma) phases of the Al₂O₃ particles. The results of mechanical behavior tests showed marked improvement in the mechanical properties of the resulted composite material, especially at 1.5%, compared with polymer blend material without nano powder addition. The tensile properties improved about (24 and 14.9) % and bending resistance about (23.5 and 16.8) % and hardness by (25 and 22) % when adding particles of size (63.8 and 68.6) respectively. Therefore, this reflects the efficiency of the proposed method to manufacture the nanocomposite powder and the possibility of using this powder as a strengthening material for the composite materials and using these composite materials in bio applications, especially in the fabrication of artificial limbs.     

激光制备多层结构的软质基底耐磨类金刚石膜

为提高金属铜软基底的耐磨、抗蚀能力，采用脉冲激光沉积技术制备了金属铜基底上的多层结构类金刚石保护膜；其中的碳化硅-类金刚石循环层避免了类金刚石膜层中内应力的累积，降低了功能类金刚石层破裂的风险，碳化硅持力层降低了软质铜基底与高硬度类金刚石层的硬度差，金属钛层则使得铜基底与上层碳化硅层牢固结合。实验测试表明，多层结构类金刚石保护膜在铜基底上附着牢固，可通过美军标MIL-48497A规定的重摩擦和国军标GJB150.5A-2009规定的高低温冲击试验，同时能够承受弱碱溶液的腐蚀；摩擦系数低、处于0.093以下，耐磨性能好、2 h摩擦未见磨痕。针对不同金属基底特性改进工艺，该技术可应用于存在腐蚀性环境中机械工具的抗磨保护膜。     

Synergistic effect of hybrid Himalayan Nettle/Bauhinia-vahlii fibers on physico-mechanical and sliding wear properties of epoxy composites

The cellulosic bast fibers are recognized as a justifiable and biodegradable substitute for producing moderate strength polymer composite materials because of their characteristics of renewability, eco-friendliness, and higher specific strength. Hence the aim of this research work is to fabricate Himalayan bast fibers (Nettle fiber (NF)/bauhinia vahlii fiber (BF)) based mono/hybrid epoxy composites at varying weight percentage of 2–6 wt% and evaluate the physical (void fraction and water absorption), mechanical (tensile strength, flexural strength, hardness) and sliding wear properties of as-fabricated composites. The 6 wt% NBF reinforced composites exhibited higher mechanical properties as compared to NF and BF composites with tensile strength of 34.04 MPa, flexural strength of 42.45 MPa, and hardness of 37.01 H_v respectively. The influence of various control factors (sliding velocity, NF/BF/NBF contents, normal load and sliding distance) on specific sliding wear rate of composites was evaluated by Taguchi (three factors at three levels) experimental design and the percentage contribution of these selected parameters on sliding wear performance was examined by Analysis of variance (ANOVA). The sliding wear property of as-developed composites was found to be greatly influenced by sliding velocity and the wear resistance was observed to be improved with the NF/BF/NBF contents. The wear mechanism of the as-fabricated composites has been elucidated by scanning electron microscopy analysis. The research outcomes demonstrated that the hybridization of Bauhinia vahlii fiber with Nettle fiber led to improve the mechanical and wear properties of epoxy composites.     

Microstructure and pitting corrosion of armor grade AA7075 aluminum alloy friction stir weld nugget zone-Effect of post weld heat treatment and addition of boron carbide

Friction stir welding(FSW) of high strength aluminum alloys has been emerged as an alternative joining technique to avoid the problems during fusion welding.In recent times FSW is being used for armor grade AA7075 aluminum alloy in defense,aerospace and marine applications where it has to serve in non uniform loading and corrosive environments.Even though friction stir welds of AA7075 alloy possess better mechanical properties but suffer from poor corrosion resistance.The present work involves use of retrogression and reaging(RRA) post weld heat treatment to improve the corrosion resistance of welded joints of aluminum alloys.An attempt also has been made to change the chemical composition of the weld nugget by adding B4C nano particles with the aid of the FSW on a specially prepared base metal plate in butt position.The effects of peak aged condition(T6),RRA and addition of B4C nano particles on microstructure,hardness and pitting corrosion of nugget zone of the friction stir welds of AA7075 alloy have been studied.Even though RRA improved the pitting corrosion resistance,its hardness was slightly lost.Significant improvement in pitting corrosion resistance was achieved with addition of boron carbide powder and post weld heat treatment of RRA.     

纳米复合自修复添加剂发动机台架试验研究

通过WD615．67行车用6缸柴油机发动机台架试验,研究了含有纳米铜材料的纳米复合添加剂对发动机动力性能的影响,试验前后对发动机主要摩擦副尺寸进行了测量。结果表明,纳米复合添加剂对发动机不同材料的摩擦副均有较好的抗磨效果,特别是在缸套等摩擦部位出现了“负磨损”,实现了摩擦副表面的原位动态自修复。添加纳米复合添加剂后有效地降低了比油耗,减少了机械功率损失, 提高了发动机的功率,改善了发动机的动力性能。     

Influence of tool pin profile on microstructure and corrosion behaviour of AA2219 Al-Cu alloy friction stir weld nuggets

To overcome the problems of fusion welding of aluminium alloys, the friction stir welding(FSW) is recognized as an alternative joining method to improve the mechanical and corrosion properties. Tool profile is one of the important variables which affect the performance of the FS weld. In the present work, the effect of tool profile on the weld nugget microstructure and pitting corrosion of AA2219 aluminium-copper alloy was studied. FSW of AA2219 alloy was carried out using five profiles, namely conical, square, triangle, pentagon and hexagon. The temperature measurements were made in the region adjacent to the rotating pin. It was observed that the peak temperature is more in hexagonal tool pin compared to the welds produced with other tool pin profiles. It is observed that the extensive deformation experienced at the nugget zone and the evolved microstructure strongly influences the hardness and corrosion properties of the joint during FSW. It was found that the microstructure changes like grain size, misorientation and precipitate dissolution during FSW influence the hardness and corrosion behaviour. Pitting corrosion resistance of friction stir welds of AA2219 was found to be better for hexagon profile tool compared to other profiles, which was attributed to material flow and strengthening precipitate morphology in nugget zone. Higher amount of heat generation in FS welds made with hexagonal profile tool may be the reason for greater dissolution of strengthening precipitates in nugget zone.     

无人机电磁弹射器的综合制动方法

利用直线电机实现无人机在短距离内可控地加速起飞已是固定翼无人机弹射起飞一种新的发展方向。为了使飞机分离后弹射台能在较短距离里完成制动,提出了直线电机弹射轨道末段定子实铁心涡流制动、运用Halbach永磁体阵列的涡流制动和橡胶阻尼制动等三种方式的综合方案,并分别对它们进行了分析计算。当弹射台的速度大于10m/s时,定子实铁心产生的涡流制动效果明显,当弹射台的速度低于3m/s时,定子实铁心涡流制动产生的制动力将迅速下降。Halbach永磁体阵列的涡流制动方式在飞机分离点开始实施,可以增加30%以上的制动效果。通过模型分析和碰撞试验,橡胶阻尼制动作为最后一级制动方式,能够有效吸收能量,实现在较短距离里的制动。     

电刷镀Cu／Ni多层膜的摩擦学性能研究

采用电刷镀法制备了Cu／Ni多层膜,对多层膜的摩擦学性能进行了研究。结果表明,电刷镀法制备Cu/Ni多层膜镀层平整、均匀致密、晶粒细小,界面清晰;多层膜的摩擦磨损性能直接由单层膜厚决定:随着单层膜厚的减小,多层膜的摩擦系数减小,磨损形式由磨料磨损逐渐转变为粘着磨损;多层膜的磨损量随单层膜厚的减小而减小,当单层膜厚减小至纳米尺度时,存在一磨损量的最小值;电刷镀 Cu／Ni多层膜的临界单层膜厚约为20 nm。     

环烷酸铅作为润滑油添加剂的摩擦学性能研究

环烷酸铅具有良好的抗磨损能力和减摩性能，其中含铅量为２０％的环烷酸铅添加剂使基础油的抗磨性能提高４０％，减摩性能提高３０％。ＳＥＭ分析显示钢球磨痕和犁沟较浅，且有含铅沉积物生成。由此推断出有机铅盐在摩擦副表面形成吸附膜，且部分吸附膜发生摩擦化学反应，产生了其有抗磨减摩作用的铅氧化物转化膜，从而起到了改善摩擦磨损性能的作用。     

Statistical variability and fragility assessment of ballistic perforation of steel plates for 7.62 mm AP ammunition

The paper describes field test results of 7.62 × 51 mm M61 AP (armour piercing) ammunition fired into mild steel targets at an outdoor range. The targets varied from 10 mm to 32 mm in thickness. The tests recorded penetration depth, probability of perforation (i.e., complete penetration), muzzle and impact velocities, bullet mass, and plate yield strength and hardness. The measured penetration depth exhibited a variability of approximately ±12%. The paper then compared ballistic test results with predictive models of steel penetration depth and thickness to prevent perforation. Statistical parameters were derived for muzzle and impact velocity, bullet mass, plate thickness, plate hardness, and model error. A Monte-Carlo probabilistic analysis was then developed to estimate the probability of plate perforation of 7.62 mm M61 AP ammunition for a range of impact velocities, and for mild steels, and High Hardness Armour (HHA) plates. This perforation fragility analysis considered the random variability of impact velocity, bullet mass, plate thickness, plate hardness, and model error. Such a probabilistic analysis allows for reliability-based design, where, for example, the plate thickness with 95% reliability (i.e. only 1 in 20 shots will penetrate the wall) can be estimated knowing the probabilistic distribution of perforation. Hence, it was found that the plate thickness to ensure a low 5% probability of perforation needs to be 11–15% thicker than required to have a 50/50 chance of perforation for mild steel plates. Plates would need to be 20–30% thicker if probability of perforation is reduced to zero.     

Friction welding of AA6061 to AISI 4340 using silver interlayer

The present work pertains to the study on joining of AA6061 and AISI 4340 through continuous drive friction welding. The welds were evaluated by metallographic examination, X-ray diffraction, electron probe microanalysis, tensile test and microhardness. The study reveals that the presence of an intermetallic compound layer at the bonded interface exhibits poor tensile strength and elongation. Mg in AA6061 near to the interface is found to be favourable for the formation and growth of Fe2Al5 intermetallics. Introduction of silver as an interlayer through electroplating on AISI 4340 resulted in accumulation of Si at weld interface, replacing Mg at AA6061 side, thereby reducing the width of intermetallic compound layer and correspondingly increasing the tensile strength. Presence of silver at the interface results in partial replacement of Fe-Al based intermetallic compounds with Ag-Al based compounds. The presence of these intermetallics was confirmed by X-ray diffraction technique. Since Ag-Al phases are ductile in nature, tensile strength is not deteriorated and the silicon segregation at weld interface on AA6061 in the joints with silver interlayer acts as diffusion barrier for Fe and further avoids formation of Fe-Al based intermetallics. A maximum tensile strength of 240 MPa along with 4.9% elongation was obtained for the silver interlayer dissimilar metal welds. The observed trends in tensile properties and hardness were explained in relation to the microstructure.