Comparative study on transverse shrinkage,mechanical and metallurgical properties of AA2219 aluminium weld joints prepared by gas tungsten arc and gas metal arc welding processes

Aluminium alloy AA2219 is a high strength alloy belonging to 2000 series. It has been widely used for aerospace applications, especially for construction of cryogenic fuel tank. However, arc welding of AA2219 material is very critical. The major problems that arise in arc welding of AA2219 are the adverse development of residual stresses and the re-distribution as well as dissolution of copper rich phase in the weld joint.These effects increase with increase in heat input. Thus, special attention was taken to especially thick section welding of AA2219-T87 aluminium alloy. Hence, the present work describes the 25 mm-thick AA2219-T87 aluminium alloy plate butt welded by GTAW and GMAW processes using multi-pass welding procedure in double V groove design. The transverse shrinkage, conventional mechanical and metallurgical properties of both the locations on weld joints were studied. It is observed that the fair copper rich cellular(CRC) network is on Side-A of both the weldments. Further, it is noticed that, the severity of weld thermal cycle near to the fusion line of HAZ is reduced due to low heat input in GTAW process which results in non dissolution of copper rich phase. Based on the mechanical and metallurgical properties it is inferred that GTAW process is used to improve the aforementioned characteristics of weld joints in comparison to GMAW process.     

Variation of chemical composition of high strength low alloy steels with different groove sizes in multi-pass conventional and pulsed current gas metal arc weld depositions

25 mm thick micro-alloyed HSLA steel plate is welded by multi-pass GMAW and P-GMAW processes using conventional V-groove and suitably designed narrow gap with 20 mm(NG-20) and 13 mm(NG-13) groove openings.The variation of weld metal chemistry in the multi pass GMA and P-GMA weld depositions are studied by spark emission spectroscopy.It is observed that the narrow groove GMA weld joint shows significant variation of weld metal chemistry compared to the conventional V-groove GMA weld joint since the dilution of base metal extends from the deposit adjacent to groove wall to weld center through dissolution by fusion and solid state diffusion.Further,it is noticed that a high rate of metal deposition along with high velocity of droplet transfer in P-GMAW process enhances the dilution of weld deposit and accordingly varies the chemical composition in multi-pass P-GMA weld deposit.Lower angle of attack to the groove wall surface along with low heat input in NG-13 weld groove minimizes the effect of dissolution by fusion and solid state diffusion from the deposit adjacent to groove wall to weld center.This results in more uniform properties of NG-13 P-GMA weld in comparison to those of NG-20 and CG welds.     

Effect of fusion welding processes on tensile properties of armor grade,high thickness,non-heat treatable aluminium alloy joints

AA5059 is one of the high strength armor grade aluminium alloy that finds its applications in the military vehicles due to the higher resistance against the armor piercing (AP) threats. This study aimed at finding the best suitable process among the fusion welding processes such as gas tungsten arc welding (GTAW) and gas metal arc welding (GMAW) by evaluating the tensile properties of AA5059 aluminium alloy joints. The fracture path was identified by mapping the low hardness distribution profile (LHDP) across the weld cross section under tensile loading. Optical and scanning electron microscopies were used to characterize the microstructural features of the welded joints at various zones. It is evident from the results that GTAW joints showed superior tensile properties compared to GMAW joints and this is primarily owing to the presence of finer grains in the weld metal zone (WMZ) and narrow heat-affected zone (HAZ). The lower heat input associated with the GTAW process effectively reduced the size of the WMZ and HAZ compared to GMAW process. Lower heat input of GTAW process results in faster cooling rate which hinders the grain growth and reduces the evaporation of magnesium in weld metal compared to GMAW joints. The fracture surface of GTAW joint consists of more dimples than GMAW joints which is an indication that the GTAW joint possess improved ductility than GMAW joint.     

Characterization of magnetically impelled arc butt welded T11 tubes for high pressure applications

Magnetically impelled arc butt(MIAB) welding is a pressure welding process used for joining of pipes and tubes with an external magnetic field affecting arc rotation along the tube circumference. In this work, MIAB welding of low alloy steel(T11) tubes were carried out to study the microstructural changes occurring in thermo-mechanically affected zone(TMAZ). To qualify the process for the welding applications where pressure could be up to 300 bar, the MIAB welds are studied with variations of arc current and arc rotation time. It is found that TMAZ shows higher hardness than that in base metal and displays higher weld tensile strength and ductility due to bainitic transformation. The effect of arc current on the weld interface is also detailed and is found to be defect free at higher values of arc currents. The results reveal that MIAB welded samples exhibits good structural property correlation for high pressure applications with an added benefit of enhanced productivity at lower cost.The study will enable the use of MIAB welding for high pressure applications in power and defence sectors.     

Effect of welding processes and consumables on fatigue crack growth behaviour of armour grade quenched and tempered steel joints

Quenched and Tempered (Q&T) steels are widely used in the construction of military vehicles due to its high strength to weight ratio and high hardness. These steels are prone to hydrogen induced cracking (HIC) in the heat affected zone (HAZ) after welding. The use of austenitic stainless steel (ASS) consumables to weld the above steel was the only available remedy because of higher solubility for hydrogen in austenitic phase. The use of stainless steel consumables for a non-stainless steel base metal is not economical. Hence, alternate consumables for welding Q&T steels and their vulnerability to HIC need to be explored. Recent studies proved that low hydrogen ferritic steel (LHF) consumables can be used to weld Q&T steels, which can give very low hydrogen levels in the weld deposits. The use of ASS and LHF consumables will lead to distinct microstructures in their respective welds. This microstructural heterogeneity will have a drastic influence in the fatigue crack growth resistance of armour grade Q&T steel welds. Hence, in this investigation an attempt has been made to study the influence of welding consumables and welding processes on fatigue crack growth behaviour of armour grade Q&T Steel joints. Shielded metal arc welding (SMAW) and Flux cored arc welding (FCAW) were used for fabrication of joints using ASS and LHF consumables. The joints fabricated by SMAW process using LHF consumable exhibited superior fatigue crack growth resistance than all other joints.     

Optimization of process parameters of the activated tungsten inert gas welding for aspect ratio of UNS S32205 duplex stainless steel welds

The activated TIG (ATIG) welding process mainly focuses on increasing the depth of penetration and the reduction in the width of weld bead has not been paid much attention. The shape of a weld in terms of its width-to-depth ratio known as aspect ratio has a marked influence on its solidification cracking tendency. The major influencing ATIG welding parameters, such as electrode gap, travel speed, current and voltage, that aid in controlling the aspect ratio of DSS joints, must be optimized to obtain desirable aspect ratio for DSS joints. Hence in this study, the above parameters of ATIG welding for aspect ratio of ASTM/UNS S32205 DSS welds are optimized by using Taguchi orthogonal array (OA) experimental design and other statistical tools such as Analysis of Variance (ANOVA) and Pooled ANOVA techniques. The optimum process parameters are found to be 1 mm electrode gap, 130 mm/min travel speed, 140 A current and 12 V voltage. The aspect ratio and the ferrite content for the DSS joints fabricated using the optimized ATIG parameters are found to be well within the acceptable range and there is no macroscopically evident solidification cracking.     

焊接过程对焊接残余应力及残余变形的影响

采用热弹塑性有限元法 ,对直通焊和多人同时分段焊两种焊接过程的平板对接焊时焊接应力变形和圆柱壳板环缝的焊接变形进行比较 ,认为多人同时分段焊较直通焊无论在降低焊接残余应力还是焊接残余变形都具有非常显著的效果     

Feasibility of surface-coated friction stir welding tools to join AISI 304 grade austenitic stainless steel

An attempt is made to develop the tools that are capable enough to withstand the shear, impact and thermal forces that occur during friction stir welding of stainless steels. The atmospheric plasma spray and plasma transferred arc hardfacing processes are employed to deposit refractory ceramic based composite coatings on the Inconel 738 alloy. Five different combinations of self-fluxing alloy powder and 60% ceramic reinforcement particulate mixtures are used for coating. The best friction stir welding tool selected based on tool wear analysis is used to fabricate the austenitic stainless steel joints.     

Effect of welding processes on mechanical and microstructural characteristics of high strength low alloy naval grade steel joints

Naval grade high strength low alloy(HSLA) steels can be easily welded by all types of fusion welding processes. However, fusion welding of these steels leads to the problems such as cold cracking, residual stress, distortion and fatigue damage. These problems can be eliminated by solid state welding process such as friction stir welding(FSW). In this investigation, a comparative evaluation of mechanical(tensile, impact,hardness) properties and microstructural features of shielded metal arc(SMA), gas metal arc(GMA) and friction stir welded(FSW) naval grade HSLA steel joints was carried out. It was found that the use of FSW process eliminated the problems related to fusion welding processes and also resulted in the superior mechanical properties compared to GMA and SMA welded joints.     

焊接工艺对熔敷金属韧性的影响

探讨了改变焊接工艺对焊条熔敷金属冲击韧性的影响．研究表明：改变焊接工艺,将通过改变熔敷金属的化学成分,影响熔敷金属的强度和韧性;降低焊接线能量时,将降低熔敷金属中的氧含量及其氧化夹杂物的数量和大小,从而提高熔敷金属的韧性     

无电焊接中厚度钢板焊接接头的组织结构与性能研究

采用无电焊接方法对12mm厚度钢板进行了焊接。分析了满足中厚度钢板焊接能量要求的技术途径;利用SEM,EDS,XRD等手段观察、分析了焊缝的组织成分与显微结构;测试了焊接接头的拉伸强度、弯曲强度、显微硬度等力学性能。结果表明:在选择高放热体系基础上,通过增大焊接笔直径、减小反应物料粒径、提高压坯密度等方法,可以有效增大焊接热效率,从而满足中厚度钢板焊接能量需求;焊缝组织分为热影响区、熔合区与合金区,焊缝合金与母材间通过熔合区形成了冶金结合;焊接接头因固溶强化和析晶强化的作用,具有良好的力学性能,拉伸强度、平均显微硬度与弯曲强度分别为357MPa、186HV0.2与644MPa,达到了野战应急抢修技术要求。     

Gas tungsten arc welding of ZrB_2-SiC based ultra high temperature ceramic composites

The difficulty in fabricating the large size or complex shape limits the application of ZrB2-SiC composites. Joining them by fusion welding without or with preheating, controlled cooling under protective gas shield leads to thermal shock failure or porosity at the weld interface. In the present work, a filler material of(ZrB2-SiC-B4C-YAG) composite with oxidation resistance and thermal shock resistance was produced in the form of welding wire. Using the filler, gas tungsten arc welding(GTAW) was performed without employing preheating, post controlled cooling and extraneous protective gas shield to join hot pressed ZrB2-SiC(ZS), and pressureless sintered ZrB2-SiC-B4C-YAG(ZSBY) composites to themselves. The fusion welding resulted in cracking and non-uniform joining without any filler material. The weld interfaces of the composites were very clean and coherent. The Vickers micro-hardness across the weld interface was found to increase due to the increase in the volume % of both SiC and B4C in the filler material. The shear strength of the weld was about 50% of the flextural strength of the parent composite.     

无电焊接热循环测试研究

利用热电偶测试了无电焊接过程中同一厚度钢板不同位置、不同厚度钢板同一位置处的焊接热循环曲线,探讨了无电焊接热循环规律及焊接母材厚度对无电焊接热循环的影响。研究表明：无电焊接时,焊件上不同位置点的热循环曲线与电弧焊基本相似。但相较而言,无电焊接在加热阶段的升温速度与冷却阶段的降温速度均显著小于电弧焊。无电焊接过程中,焊件上离焊缝中心线越近,其升温速度越大,峰值温度越高,冷却速度也越大,这一变化规律与电弧焊时完全一致。无电焊接时,焊接热量沿横向的传热速度远大于其沿纵向的传热速度,这使得焊件厚度对无电焊接的影响较为显著,也是焊件厚度增加将导致焊接难度显著增大的根本原因。     

LD10cs 铝合金焊接接头疲劳裂纹扩展速率的研究

本文研究用表面裂纹法测试LD10cs铝合金板材焊接接头各部位疲劳裂纹扩展速率。结果表明:焊接接头各部位疲劳裂纹扩展速率随焊接热循环引起的金属组织变化而变化,有一定规律性。熔合线和焊趾处疲劳裂纹扩展速率较其他部位大。焊缝加强高的存在,引起焊趾处应力集中,使该处疲劳性能进一步恶化,成为焊接接头疲劳性能最差的部位。结合金相组织和扫描电镜分析,对影响焊接接头各部位疲劳裂纹扩展速率的各种因素作了较详细的探讨,并提出了改进焊缝质量的建议。     

Influence of magnetically constricted arc traverse speed (MCATS) on tensile properties and microstructural characteristics of welded Inconel 718 alloy sheets

The magnetically constricted arc technique was implemented to mitigate the heat input related metal-lurgical problems in Gas Tungsten Arc Welding (GTAW) of Inconel 718 alloy particularly Nb segregation and subsequent laves phase evolution in fusion zone. This paper reports the direct effect of magnetically constricted arc traverse speed (MCATS) on bead profile, tensile properties and microstructural evolution of Inconel 718 alloy sheets joined by Gas Tungsten Constricted Arc Welding (GTCAW) process. The mechanism amenable for the microstructural modification and corresponding influence on the tensile properties of joints is investigated both in qualitative and quantitative manner related to the mechanics of arc constriction and pulsing. It is correlated to the solidification conditions during welding. The relationship between MCATS and Arc Constriction Current (ACC) was derived. Its interaction effect on the magnetic arc constriction and joint performance was analysed. Results showed that the joints fabricated using CATS of 70 mm/min exhibited superior tensile properties (98.39% of base metal strength with 31.50% elongation). It is attributed to the grain refinement in fusion zone microstructure leading to the evolution of finer, discrete laves phase in interdendritic areas.     

焊接工艺对GMAW堆焊焊缝区温度场影响的数值模拟

为了探索焊接工艺对熔化极气体保护堆焊快速成形零件组织性能的影响，根据材料热物理性能参数以及相变潜热与温度的非线性关系，建立了熔化极气体保护堆焊成形过程的数学模型和有限元模型，利用ANSYS软件的APDL语言编写程序，实现了高斯移动热源载荷下的熔化极气体保护堆焊成形温度场计算，分析对比了不同焊接工艺对焊缝区温度场热循环的影响。结果表明：在其他因素一定的条件下，热输入和焊接速度对焊缝区热循环影响显著，而基板厚度对其影响较小；选择厚度约为16mm的基板，采用小于120×20J的热输入和大于10mm／s的焊接速度有望成形出性能优良的零件。     

Microstructure and pitting corrosion of armor grade AA7075 aluminum alloy friction stir weld nugget zone-Effect of post weld heat treatment and addition of boron carbide

Friction stir welding(FSW) of high strength aluminum alloys has been emerged as an alternative joining technique to avoid the problems during fusion welding.In recent times FSW is being used for armor grade AA7075 aluminum alloy in defense,aerospace and marine applications where it has to serve in non uniform loading and corrosive environments.Even though friction stir welds of AA7075 alloy possess better mechanical properties but suffer from poor corrosion resistance.The present work involves use of retrogression and reaging(RRA) post weld heat treatment to improve the corrosion resistance of welded joints of aluminum alloys.An attempt also has been made to change the chemical composition of the weld nugget by adding B4C nano particles with the aid of the FSW on a specially prepared base metal plate in butt position.The effects of peak aged condition(T6),RRA and addition of B4C nano particles on microstructure,hardness and pitting corrosion of nugget zone of the friction stir welds of AA7075 alloy have been studied.Even though RRA improved the pitting corrosion resistance,its hardness was slightly lost.Significant improvement in pitting corrosion resistance was achieved with addition of boron carbide powder and post weld heat treatment of RRA.     

Microstructure,mechanical and corrosion behavior of high strength AA7075aluminium alloy friction stir welds-Effect of post weld heat treatment

High strength aluminium alloy AA7075(Al-Zn-Mg-Cu) is a precipitate hardenable alloy widely used in the aerospace,defense,marine and automobile industries.Use of the heat treatable aluminium alloys in all these sectors is ever-increasing owing to their excellent strength-toweight ratio and reasonably good corrosion resistance.The shortage in corrosion resistance,however,usually poses negative concern about their reliability and lifetime when they service in the variable marine environments.These alloys also exhibit low weldability due to poor solidification microstructure,porosity in fusion zone and lose their mechanical properties when they are welded by fusion welding techniques.Friction stir welding(FSW) is a reliable technique to retain the properties of the alloy as the joining takes place in the solid state.The welds are susceptible to corrosion due to the microstructural changes in the weld nugget during FSW.In this work,the effect of post weld treatments,viz.,peak aging(T6) and retrogression reaging(RRA),on the microstructure,mechanical properties and pitting corrosion has been studied.Friction stir welding of 8 mm-thick AA7075 alloy was carried out.The microstructural changes of base metal and nugget zone of friction stir welds were studied using optical microscopy,scanning electron microscopy and transmission electron microscopy.Tensile and hardness test of base metal and welds has been carried out.Pitting corrosion resistance was determined through dynamic polarization test.It was observed that the hardness and strength of weld were observed to be comparatively high in peak aged(T6) condition but the welds showed poor corrosion resistance.The resistance to pitting corrosion was improved and the mechanical properties were maintained by RRA treatment.The resistance to pitting corrosion was improved in RRA condition with the minimum loss of weld strength.     

Gas metal arc welding of high nitrogen stainless steel with Ar-N2-O2 ternary shielding gas

High nitrogen stainless steel with nitrogen content of 0.75％was welded by gas metal arc welding with Ar—N2-O2 ternary shielding gas. The effect of the ternary shielding gas on the retention and improvement of nitrogen content in the weld was identified. Surfacing test was conducted first to compare the ability of O2 and CO2 in prompting nitrogen dissolution. The nitrogen content of the surfacing metal with O2 is slightly higher than CO2. And then Ar—N2-O2 shielding gas was applied to weld high nitrogen stainless steel. After using N2-containing shielding gas, the nitrogen content of the weld was improved by 0.1 wt％. As N2 continued to increase, the increment of nitrogen content was not obvious, but the ferrite decreased from the top to the bottom. When the proportion of N2 reached 20％, a full austenitic weld was obtained and the tensile strength was improved by 8.7％. Combined with the results of surfacing test and welding test, it is concluded that the main effect of N2 is to inhibit the escape of nitrogen and suppress the ni-trogen diffusion from bottom to the top in the molten pool.     

Investigation on the process parameters of TIG-welded aluminum alloy through mechanical and microstructural characterization

Multi-pass TIG welding was conducted on plates (15×300×180 mm3) of aluminum alloy Al-5083 that usually serves as the component material in structural applications such as cryogenics and chemical processing industries. Porosity formation and solidification cracking are the most common defects when TIG welding Al-5083 alloy, which is sensitive to the welding heat input. In the experiment, the heat input was varied from 0.89 kJ/mm to 5 kJ/mm designed by the combination of welding torch travel speed and welding current. Tensile, micro-Vicker hardness and Charpy impact tests were executed to witness the impetus response of heat input on the mechanical properties of the joints. Radiographic inspection was performed to assess the joint's quality and welding defects. The results show that all the specimens displayed inferior mechanical properties as compared to the base alloy. It was established that porosity was progressively abridged by the increase of heat input. The results also clinched that the use of me-dium heat input (1-2 kJ/mm) offered the best mechanical properties by eradicating welding defects, in which only about 18.26% of strength was lost. The yield strength of all the welded specimens remained unaffected indicated no influence of heat input. Partially melted zone (PMZ) width also affected by heat input, which became widened with the increase of heat input. The grain size of PMZ was found to be coarser than the respective grain size in the fusion zone. Charpy impact testing revealed that the absorbed energy by low heat input specimen (welded at high speed) was greater than that of high heat input (welded at low speed) because of low porosity and the formation of equiaxed grains which induce better impact toughness. Cryogenic (-196 C) impact testing was also performed and the results corroborate that impact properties under the cryogenic environment revealed no appreciable change after welding at designated heat input. Finally, Macro and micro fractured surfaces of tensile and impact specimens were analyzed using Stereo and Scanning Electron Microscopy (SEM), which have supported the experimental findings.