溶胶一凝胶法制备二氧化钛及其转化为氮化钛的研究

本文以钛酸丁酯为原料，通过溶胶一凝胶法制备了ＴｉＯ２凝胶，在高温下烧结此凝胶得到ＴｉＯ２。将ＴｉＯ２粉末在９００°Ｃ以上用氨进行氮化，制得金黄色的氮化钛。通过使用热分析、色谱分析、扫描电镜及Ｘ一射线衍射等手段，研究并揭示了凝胶在陶瓷化生成ＴｉＯ２的过程中的化学反应，结晶及晶型随温度的变化规律。发现了氮化钛陶瓷的生成率与ＴｉＯ２溶胶的制备条件之间的关系。     

多铁性磁电智能复合材料的力学研究进展

介绍了多铁性磁电智能复合材料的概念、分类及发展现状;总结了两类典型多铁性复合材料的力学问题（包括波动与振动问题、夹杂问题、断裂问题等）的研究进展;分析了层状多铁性复合材料力学行为的特殊性;基于应变介导的磁电耦合机制,阐述了界面断裂力学研究对于层状多铁性复合材料研制的重要性和必要性;最后指出了该领域下一步的研究方向。     

Prediction of three-dimensional elastic behavior of filament-wound composites based on the bridging model

This work provides a method to predict the three-dimensional equivalent elastic properties of the filament-wound composites based on the multi-scale homogenization principle.In the meso-scale,a representative volume element(RVE)is defined and the bridging model is adopted to establish a theoretical predictive model for its three-dimensional equivalent elastic constants.The results obtained through this method for the previous experimental model are compared with the ones gained respec-tively by experiments and classical laminate theory to verify the reliability of this model.In addition,the effects of some winding parameters,such as winding angle,on the equivalent elastic behavior of the filament-wound composites are analyzed.The rules gained can provide a theoretical reference for the optimum design of filament-wound composites.     

气囊辅助RTM制备复合材料承力筒内腔尺寸控制技术

根据气囊充压压力与复合材料承力筒内径之间的变化关系,给出了成型复合材料承力筒内表面的气囊尺寸计算方程。分析了气囊充压压力增大对承力筒的壁厚、纤维含量和弯曲性能的影响。采用气囊辅助RTM工艺整体制备出复合材料承力筒。试验结果表明,气囊充压压力使复合材料承力筒的壁厚减薄,纤维体积含量增加,弯曲性能提高;选择适当的气囊充压压力可以制备出满足设计要求的复合材料承力筒。     

聚硅氧烷先驱体转化制备2D Cf/Si-O-C材料

以二维碳纤维布和廉价的聚硅氧烷为原料,采用先驱体转化工艺制备2D Cf/Si-O-C材料,对其力学性能进行了考察,并与以聚碳硅烷为先驱体制备的2D Cf/SiC材料在价格和性能方面进行了对比。实验表明,2D Cf/Si-O-C材料力学性能较2D Cf/SiC材料有所下降,但成本大大降低。2D Cf/Si-O-C材料弯曲强度达到157.9 MPa,断裂韧性达到8.4MPa.m1/2,剪切强度达到23.4MPa,并且在1400℃下能较好保持材料的力学性能。     

Si3 N4基复相陶瓷天线罩材料的制备及性能

基于高马赫数导弹天线罩为应用背景,以Si粉、BN粉、SiO2粉为主要原料,采用反应烧结法制备Si3N4基复相陶瓷材料,探讨了原料组成、成型工艺及坯体密度对材料性能的影响。试验结果表明:当原料中Si、BN和SiO2分别为55%、30%和10%时,材料强度可达96.7MPa,断裂韧性可达1.80MPa.m1/2。同时材料具有良好的介电性能及热物理性能。     

Investigation of the mechanical and ballistic properties of hybrid carbon/ aramid woven laminates

High-performance ballistic fibers, such as aramid fiber and ultra-high-molecular-weight polyethylene (UHMWPE), are commonly used in anti-ballistic structures due to their low density, high tensile strength and high specific modulus. However, their low modulus in the thickness direction and insufficient shear strength limits their application in certain ballistic structure. In contrast, carbon fiber reinforced epoxy resin matrix composites (CFRP) have the characteristics of high modulus in the thickness direction and high shear resistance. However, carbon fibers are rarely used and applied for protection purposes. A hybridization with aramid fiber reinforced epoxy resin matrix composites (AFRP) and CFRP has the potential to improve the stiffness and the ballistic property of the typical ballistic fiber composites. The hybrid effects on the flexural property and ballistic performance of the hybrid CFRP/AFRP laminates were investigated. Through conducting mechanical property tests and ballistic tests, two sets of reliable simulation parameters for AFRP and CFRP were established using LS-DYNA software, respectively. The experimental results suggested that by increasing the content of CFRP that the flexural properties of hybrid CFRP/AFRP laminates were enhanced. The ballistic tests’ results and the simulation illustrated that the specific energy absorption by the perforation method of CFRP achieved 77.7% of AFRP. When CFRP was on the striking face, the shear resistance of the laminates and the resistance force to the projectiles was promoted at the initial penetration stage. The proportion of fiber tensile failures in the AFRP layers was also enhanced with the addition of CFRP during the penetration process. These improvements resulted in the ballistic performance of hybrid CFRP/AFRP laminates was better than AFRP when the CFRP content was 20 wt% and 30 wt%.     

准陶瓷Cf/SiC复合材料的制备

采用热重-差热(TG-DTA)、红外(IR)等分析测试手段,研究了聚碳硅烷(PCS)的裂解及化学转化过程,从理论上验证了先驱体聚碳硅烷(PCS)600℃裂解产物的准陶瓷特性.先驱体聚碳硅烷在600℃呈现一种半有机、半无机状态,其产物具有准陶瓷的特征,在大约750℃出现无机化转变高峰,固称其为准陶瓷.以碳布、准三维编织体、三维编织体为增强体,采用先驱体浸渍裂解(PIP)工艺在600℃制备了碳纤维增强碳化硅(Cf/SiC)准陶瓷基复合材料.结果表明,以三维编织体增强的准陶瓷Cf/SiC复合材料获得了较理想的结构、性能,所制备3D-Cf/SiC复合材料密度仅有1.27g/cm3,弯曲强度达到193.69MPa,室温拉伸强度为197.69MPa,600℃拉伸强度为167.33MPa.复合材料断口形貌分析表明,在低温600℃制备的准陶瓷Cf/SiC复合材料呈现明显的韧性断裂特征.     

用溶胶-凝胶法制备碳纤维三维编织物增强氧化铝基复合材料的研究

本文研究了溶胶－凝胶（Ｓｏｌ－ｇｅｌ）法制备碳纤维三维编织物增强氧化铝（Ａｌ２Ｏ３）基复合材料的成型工艺及其力学性能，研究了两种主要起始物Ａｌ（ＮＯ３）３、ＡｌＣｌ３配制的氧化铝溶胶对复合材料成型工艺和力学性能的影响。分别以Ａｌ（ＮＯ３）３和ＡｌＣｌ３为起始物，制备得到Ⅰ＃、Ｉ＃复合材料。研究表明，以Ａｌ（ＮＯ３）３为起始物配制的溶胶粘度较小，利于材料的致密化。经过溶胶浸渍、凝胶、裂解１３个周期后，Ⅰ＃材料的密度和室温三点弯曲强度分别为１．８６ｇ／ｃｍ３和１４５．２ＭＰａ，而ＩＩ＃材料的密度和室温三点弯曲强度分别为１．６３ｇ／ｃｍ３和１０４．１ＭＰａ，材料均呈典型的韧性断裂模式。用扫描电子显微镜（ＳＥＭ）观察试样的断口形貌，发现断口表面有大量的纤维拔出，纤维表现了较好的增韧效果。     

RTM工艺整体成型复合材料连接裙轴压性能

整体成型的固体火箭发动机复合材料连接裙有助于连接裙的减重及其使用性能的提高。本文采用RTM工艺制备出了全复合材料整体连接裙并对其进行了轴压承载性能考核。试验结果表明,RTM工艺整体成型的复合材料连接裙质量均匀,在设计载荷作用下,连接裙的轴向应变远小于0.5%的复合材料许用应变指标,连接裙的轴向表观结构刚度为40.9GPa。